【摘 要】
：
设计了结晶器可旋转的电渣炉,研究了旋转速率对电渣锭致密度的影响。结果表明,当结晶器的旋转速率从0增加到28r/min时,电渣锭的致密度显著提高,从77%提高到94%,且组织分布更
论文部分内容阅读
设计了结晶器可旋转的电渣炉,研究了旋转速率对电渣锭致密度的影响。结果表明,当结晶器的旋转速率从0增加到28r/min时,电渣锭的致密度显著提高,从77%提高到94%,且组织分布更加均匀;而当旋转速率达到35r/min时,致密度反而降至91%,这说明结晶器适当的运动可以改善钢锭的凝固组织。
A mold-rotatable electroslag furnace was designed and the effect of rotation rate on the densification of the electroslag was studied. The results show that the density of the electroslag ingot significantly increases from 77% to 94% with a more uniform distribution of the microstructure when the rotation rate of the mold increases from 0 to 28 r / min. When the rotation rate reaches 35 r / min , But the density decreased to 91%, indicating that proper mold movement can improve the ingot solidified tissue.
其他文献
利用数码相机、X射线衍射仪、材料试验机及扫描电镜研究了磁感应强度为0~1.11T的直流磁场对纯镁凝固组织、结晶织构及力学性能的影响。结果表明,随着直流磁感应强度的增加,纯
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
通过恒应变速率超塑性拉伸试验,研究了TC21钛合金在变形温度为1 153~1 193K,应变速率为3.3×10-4~3.3×10-2 s-1条件下的拉伸流变应力行为。计算了TC21钛合金超塑性拉伸变形
通过对比分析太阳能用压铸AZ91D合金在3.5％的NaC1溶液,0.5 mol/L的Na2 5O4溶液和0.5 mol/L的MgSO4溶液中的腐蚀行为,系统研究了SO4”离子对AZ91D合金腐蚀行为的影响.结果表明,
以喷射沉积技术制备出Mg-Al-Zn系合金沉积坯,对其尺寸不均匀的挤压坯在高度、厚度方向上进行性能与微观组织的不均匀性研究。结果表明,挤压坯高度方向硬度值几乎没有变化,而
研究了Fe元素对ZL114A合金疲劳行为的影响,测试了Fe含量为0.07%和0.5%时合金的疲劳极限,观察了合金在两种Fe含量下的疲劳断口。结果表明,Fe含量为0.5%时的疲劳极限比0.07%时
从体育器械用镁合金的激光表面改性角度出发,运用X射线衍射仪、光学显微镜、显微硬度仪、磨损试验机及电化学测量系统,研究了激光熔覆复合涂层对合金母材物相、显微组织、显
目的 探讨护理干预对肺结核合并糖尿病患者的影响.方法 将68例肺结核合并糖尿病患者随机分成对照组和干预组各34例.对照组给予常规护理、药物治疗,干预组在对照组的基础上给
比较了Mg-Gd-Y-Nd-Zr耐热镁合金变形后及经T5和T6处理后的组织演变。在热塑性变形过程中,合金组织内部同时发生动态再结晶和动态析出,晶粒内发生的动态析出降低了再结晶形核
研究了热处理和稀土Ce共同作用对AZ91D镁合金组织和性能的影响.结果表明,AZ91D镁合金中加入稀土Ce后,生成了杆状化合物Al4Ce,且网状分布的β-Mg17Al12相变成弥散化分布.随稀