The effect of extrusion temperature and ratio on the microstructure, hardness, compression, and corrosion behavior of Mg–5Zn–1.5Y alloy were analyzed in this study. The microstructural observations revealed that the cast alloy consists of α-Mg grains, and
【机 构】
：
Materials Engineering Department, Faculty of Materials Engineering and Interdisciplinary Science, Sh
论文部分内容阅读
The effect of extrusion temperature and ratio on the microstructure, hardness, compression, and corrosion behavior of Mg–5Zn–1.5Y alloy were analyzed in this study. The microstructural observations revealed that the cast alloy consists of α-Mg grains, and Mg3Zn6Y and Mg3Zn3Y2 intermetallic compounds, mostly located on the α-Mg grain boundaries. Extruded alloy at higher temperatures showed coarser grain microstructures, whereas those extruded at higher ratios contained finer ones, although more dynamic recrystalized grains with lower intermetallics were measured at both conditions. Combined conditions of the lower temperature (340℃) and higher ratio (1:11.5) provided higher compressive strengths. However, no significant hardness improvement was achieved. The extrusion process could decrease the corrosion rate of the cast alloy in simulated body fluid for over 80％ due to primarily the refined microstructure. The extrusion temperature showed a more pronounced effect on corrosion resistance compared to the extrusion ratio, and the higher the extrusion temperature, the higher the corrosion resistance.
其他文献
The interface characteristics of cyanide tailings are different from those of the raw ore. In this study, valuable elements could not be thoroughly recovered via the flotation of cyanide tailings from Shandong, China. The interface and floatability of the
Current electronic technology based on silicon is approaching its physical and scientific limits. Carbon-based devices have numer-ous advantages for next generation electronics (e.g., fast speed, low power consumption and simple process), that when combin
Selective laser melting (SLM), an additive manufacturing process mostly applied in the metal material field, can fabricate complex-shaped metal objects with high precision. Nickel-based superalloy exhibits excellent mechanical properties at elevated tempe
Reverse flotation desilication is an indispensable step for obtaining high-grade fluorapatite. In this work, dodecyltrimethylammoni-um bromide (DTAB) is recommended as an efficient collector for the reverse flotation separation of quartz from fluorapatite
Tribology, which is the study of friction, wear, and lubrication, largely deals with the service performance of structural materials. For example, newly emerging high-entropy alloys (HEAs), which exhibit excellent hardness, anti-oxidation, anti-softening
Combustion kinetics of the hydrochar was investigated using a multi-Gaussian-distributed activation energy model (DAEM) to ex-pand the knowledge on the combustion mechanisms. The results demonstrated that the kinetic parameters calculated by the multi-Gau
Porous materials have promise as sound insulation, heat barrier, vibration attenuation, and catalysts. Most industrial solid wastes, such as tailings, coal gangue, and fly ash are rich in silicon. Additionally, a high silicon content waste is a potential
Petroleum coke is industrial solid wastes and its disposal and storage has been a great challenge to the environment. In this study, petroleum coke was utilized as a novel co-reduction reductant of low-grade laterite ore and red mud. A ferronickel product
A new method is proposed for the recovery of Mn via the direct electrochemical reduction of LiMn2O4 from the waste of lithium-ion batteries in NaCl?CaCl2 melts at 750℃. The results show that the LiMn2O4 reduction process by the electrochemical method on t
To improve the separation capacity of uranium in aqueous solutions, 3R-MoS2 nanosheets were prepared with molten salt electro-lysis and further modified with polypyrrole (PPy) to synthesize a hybrid nanoadsorbent (PPy/3R-MoS2). The preparation conditions