The influence of submerged entry nozzle clogging on the behavior of molten steel in continuously cast slab molds was studied using commercial code CFX4.3. The results indicate that clogging at the top part of the nozzle port not only increases the velocity of molten steel, but also enhances the wall shear stress, F number and heat flux. This clogging has the greatest effect on the behavior of molten steel. However, clogging at the top 1/3 of the nozzle only increases the velocity of molten steel and has little influence. Clogging at the bottom of the nozzle almost has no influence.
The influence of submerged entry nozzle clogging on the behavior of molten steel in continuously cast slab molds was studied using commercial code CFX4.3. The results indicate that clogging at the top part of the nozzle port not only increases the velocity of molten steel, but This clogging has the greatest effect on the behavior of molten steel. However, clogging at the greatest effect on the behavior of molten steel. However, clogging at the greatest effect on the behavior of molten steel. However, clogging at the greatest effect on the behavior of molten steel. Clogging at the bottom of the nozzle almost has no influence.