(1S,2S)-DPEN修饰的负载型钌-铑双金属催化剂催化苯乙酮及其衍生物的不对称加氢

来源 :物理化学学报 | 被引量 : 0次 | 上传用户:Layman_Zhejiang
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
制备了以三苯基膦(PPh_3)作为助剂的Ru-Rh/γ-Al_2O_3催化剂,在氢氧化钾的异丙醇溶液中,用(1S,2S)-DPEN[(1S,2S)-1,2-diphenylethane-1,2-diamine]作手性修饰剂对苯乙酮及其衍生物进行不对称催化加氢,此催化剂表现出较高的催化活性和良好的对映选择性.优化反应条件,苯乙酮、乙基苯基酮和异丙基苯基酮的转化率分别达到92.5%,95.9%,100%,生成(R)-构型产物的ee值分别达到79.6%、81.2%和81.4%. Ru-Rh / γ-Al_2O_3 catalyst was prepared with triphenylphosphine (PPh_3) as a promoter in a solution of (1S, 2S) -DPEN [(1S, 2S) -1 , 2-diphenylethane-1,2-diamine] as the chiral modifier for the asymmetric catalytic hydrogenation of acetophenone and its derivatives, the catalyst showed high catalytic activity and good enantioselectivity. Optimum reaction conditions , The conversions of acetophenone, ethyl phenyl ketone and isopropyl phenyl ketone reached 92.5%, 95.9% and 100%, respectively. The ee values ​​of (R) -configuration products reached 79.6%, 81.2% and 81.4%.
其他文献
采用电化学置换法,在Vulcan XC-72表面制备得到了活性高和分散性好的纳米Ptshell-Nicore电催化剂.该方法先以NaH2PO2为还原剂,化学沉积得到Ni核,Pt在Ni核表面通过原位置换形
以金鸡纳碱衍生物作为手性修饰剂,研究了三苯基膦稳定的Ir/SiO2催化剂催化芳香酮多相不对称加氢.通过电感耦合等离子体原子发射发谱(ICP-AES)、高分辨透射电镜(HRTEM)、X射线
在惰性气氛下,以Li2CO3、FeC2O4·2H2O和NH4H2PO4为原料,用高温固相方法合成了橄榄石型LiFePO4材料.利用不同升温速率的热重及差热分析研究了固相合成LiFePO4的反应动力学.研
制备了负载型催化剂Ru/ZrO2·xH2O,并用XRD、XPS和TEM对催化剂进行了表征,所制得的催化剂金属钌的平均粒径约为3.8nm.在2MPa和40℃的温和条件下,以水为溶剂时,Ru/ZrO2&#1
天然气水合物的相平衡条件一直是水合物相关研究的重点和难点.本文探讨了沉积物孔隙大小及其分布特征对水合物相平衡条件的影响机理,提出了有效孔隙半径的概念,并利用沉积物
双分子亲核(SN2)反应是重要的基本有机反应之一,其中电子从亲核基团向离去基团的转移发挥着关键作用.利用从头计算方法CCSD(T)/aug-cc-pVDZ和我们发展的分子形貌理论,对反应F
分别以戊二醛和Fe3+改性壳聚糖和海藻酸钠并分别与柔性链聚乙烯醇(PVA)共混,制备了Fe-SA-CS-GA/PVA聚合物双极膜.测定膜的红外光谱,I-V工作曲线,Na+与Cl-透过双极膜的迁移数,
以微波协助乙二醇工艺合成了碳负载不同粒径大小的PtRu/C纳米催化剂,主要考察了溶液pH值对RtRu粒子大小的影响.利用紫外可见光谱、能量散射X射线谱、透射电镜和X射线衍射谱对
以十六烷基三甲基溴化铵、十二胺为模板剂,采用双模板法及均相沉淀法,分别制备了介孔结构的SnO2.BET测试结果表明,双模板法制备的介孔SnO2平均孔径、孔容和比表面积分别为4.9
分别以柠檬酸、葡萄糖为络合剂,用溶胶-凝胶法制备了CeO_2和掺杂少量Sn的Ce-Sn-O复合氧化物,利用XRD、TPR、FT-IR、比表面法、TEM等方法表征了四种催化剂的物理化学性质,同时