The influence of rare earths (RE) on solidification behavior of a high speed steel for roll was investigated by using differential scanning calorimetry (DSC) in
【机 构】
：
State Key Laboratory of Metastable Materials Science and Technology,College of Mechanical and Engine
论文部分内容阅读
The influence of rare earths (RE) on solidification behavior of a high speed steel for roll was investigated by using differential scanning calorimetry (DSC) in combination of microstructure analysis.It was found that the sequence of solidification was L→γ,L→γ+MC,L→γ+M2C,L→γ+M6C,respectively.The start temperature and the latent heat liberated by unit mass of L→γ and L→γ+MC increased with increase of RE addition,indicating that RE could trigger the crystallization of the primary γ and the MC carbide more effectively.The promoting effect of RE on the heterogeneous nucleation was believed to be an important cause of this effect.Grain refinement,discontinuous network of eutectic carbides and disperse and finer MC were observed in the samples with RE addition,moreover,RES could act as the heterogeneous nucleus of the MC.RE addition was favorable for stable M6C at the expense of the metastable M2C.
其他文献
本文从探讨新时期医院规划设计的重要意义出发，详细阐述了医院规划设计中重要性和重要地位。接着笔者又深入分析了当前我国医院规划设计中的问题所在并就现代医院规划设计理念
Binary Ce-Zr (CZ),Pr-Zr (PZ) and ternary Ce-Zr-Pr (CZP) mixed oxides were prepared by an ammonia-aided co-precipitation method,and were aged in a steam/air flow
Er3+ and Li+ codoped Y3Al5O12 (YAG) powders were prepared for a systematic investigation of their upconversion emissions.X-ray diffraction (XRD),upconversion em
we developed a new silicate-based full-color phosphor Ba3Lu2(SiO4)3:Et2+ through solid state reaction.The host crystal structure was isostructural with Ca3Y2(Si
通过湿法球磨制备CoFe2O4-BaTiO3颗粒复合材料,研究材料成分和调制频率与电磁效应的关系.结果表明:电磁效应系数随着调制频率由400 Hz增加到1 000 Hz而增加.由于CoFe2O4的电
Nanocrystalline cubic Y2O3:Eu were prepared by combustion reaction.The crystal structure and morphology were analyzed by means of X-ray diffraction (XRD) and tr
Uniform YF3 nanorods composed ofnanoparticles were successfully prepared via a facile solvothermal method with ethanol as solvent and tetrabutyl ammonium fluori
The water repellence and mechanical properties of the gelatin/Ce(Ⅲ) fiber (GCe fiber) were improved by heat treatment,which was an easy and non-toxic method.Th
Monodispersed and water-soluble TbF3 nanoparticles were synthesized at a relatively low temperature in aqueous solution using citric acid as an additive,and cha
(Ba0.5Sr0.5)1-xPrxCo0.8Fe0.2O3-δ (BSPCFx;x=0.00-0.30) oxides were synthesized by a sol-gel thermolysis process using combination of PVA and urea,and were also