A new lead(Ⅱ) iodide coordination polymer [(npq)(PbI3)]n 1 (npq=N-propyl-quinolinium) has been synthesized in the presence of npq as structure-directing reagent (SDA). Compound 1 crystallizes in the orthorhombic system,space group Pbca,with a=19.158(4),b= 7.9909(16),c=22.929(5),V=3510.2(12)3,Z=8,Dc= 2.877 g/cm3,F(000)=2672,C12H14I3NPb,Mr=760.14,μ(MoKα)=14.872 mm-1,the final R=0.0431 and wR=0.1021 for 3678 observed reflections with I > 2σ(I). Structure determination indicates that the [PbI3]-n infinite chains in each unit cell shape the sketch of 1,which could be described as the result of face-sharing distorted PbI6 octahedra running along the b axis. Electrostatic interaction between conjugated organic counter-cations and inorganic moieties presents and contributes to the crystal packing. 1 was further characterized with IR and elemental analysis. Based on the crystal structure data,quantum chemical calculation with DFT method was used to reveal the electronic structure and optical property of 1.
A new lead (Ⅱ) iodide coordination polymer [(npq) (PbI3)] n 1 (npq = N-propyl-quinolinium) has been synthesized in the presence of npq as structure- directing reagent orthorhombic system, space group Pbca with a = 19.158 (4), b = 7.9909 (16), c = 22.929 5 V = 3510.2 123 Z = 8 Dc = 2.877 g / cm3, The final R = 0.0431 and wR = 0.1021 for 3678 were reflections with I> 2σ (I). Structure determination indicates that the [F (000) = 2672, C12H14I3NPb, Mr = 760.14, μ (MoKα) = 14.872 mm- PbI3] -n infinite chains in each unit cell shape the sketch of 1, which could be described as the result of face-sharing distorted PbI6 octahedra running along the b axis. Electrostatic interaction between conjugated organic counter-cations and inorganic moieties presents and contributes to the crystal packing. 1 was further characterized with IR and elemental analysis. Based on the crystal structure data, quantum chemical calculation with DFT method was used to reveal the electronic structure and optical property of 1.