微米级薄硅钢片（１１０）［００１］织构的形成研究了压下率及中间热处理条件对（１１０）（００！）织构形成的影响。将２．ｏｍｍ的热轧硅钢板在工作辊径２０ｍｍ及５０ｍｍ轧机上轧至１００卜ｍ厚，再进行１１５０℃Ｘｌｈ热处理，发现（１１０）异常晶粒完全没有长大...
MICROSTRUCTURE OF MICRO SILICON STEEL SHEET (110) [001] TEXTILE FORMATION The effect of reduction rate and intermediate heat treatment conditions on the texture of (110) (00!) Was studied. Will be 2 omm hot-rolled silicon steel plate in the work roll diameter 20mm and 50mm rolling mill to 100 Bu m thick, and then 1150 ℃ Xlh heat treatment and found (110) abnormal grains did not grow ...