Three-dimensionally ordered macro-porous(3DOM)Pt/TiO_2 catalysts were prepared by template and impregna- tion methods,and the resultant samples were characterized by using TG-DTA,XRD,SEM,TEM,and TPR techniques.The catalytic performance for water-gas shift(WGS)reaction was tested,and the influences of some conditions,such as reduction temperature of catalysts,the amount of Pt loadings and space velocity on catalytic performance were investigated.It was shown that Pt particles were homogeneously dispersed on 3DOM TiO_2.The reduction of TiO_2 surface was important for the catalytic performance.The activity test results showed that the 3DOM Pt/TiO_2 catalysts exhibited very good catalytic performance for WGS reaction even at high space velocity,which was owing to the better mass transfer of 3DOM porous structure besides the high intrinsic activity of Pt/TiO_2.
Three-dimensionally ordered macro-porous (3DOM) Pt / TiO_2 catalysts were prepared by a template and impregna- tion methods, and the resultant samples were characterized by using TG-DTA, XRD, SEM, TEM, and TPR techniques. The catalytic performance for water-gas shift (WGS) reaction was tested, and the influences of some conditions, such as reduction temperature of catalysts, the amount of Pt loadings and space velocity on catalytic performance were .tt shown that Pt particles were homogeneously dispersed on 3DOM TiO 2 surface was important for the catalytic performance. The activity test results showed that very good catalytic performance for WGS reaction even at high space velocity, which was due to the better mass transfer of 3DOM porous structure besides the high intrinsic activity of Pt / TiO_2.