本编辑部可提供以下专利原文 (英文 ) ,每篇收取 30元工本费。0 10 70 1ｐ叠层状晶体结构的氢氧化镁之制备 含镁盐的水溶液中加入水溶性碱性物质 ,在 10 1.32 5ｋＰａ或稍高压力和室温至 10 0℃或稍高的温度下制得氢氧化镁。所得产品最大粒度不大于 5 μｍ ,厚度约 30 0～ 5
The editorial department can provide the following original patent (English), each charged 30 yuan fee. 0 10 70 Preparation of 1p lamellar crystal structure magnesium hydroxide Water-soluble basic substance is added to the magnesium salt-containing aqueous solution at a pressure of 10 1.32 5 kPa or slightly high and room temperature to 100 ° C. or slightly higher magnesium hydroxide. The maximum particle size of the product is not more than 5 μm, the thickness of about 30 0 ~ 5