This paper reports on high-performance waveguide-integrated germanium photodiodes for optical communications applications. 200 mm wafers and production tools were used to fabricate the devices. Yields over 97% were obtained for three different compact pho
【机 构】
：
Institutd’ElectroniqueFondamentale(IEF),Univ.Paris-Sud,CNRS,Bat220,F-91405Orsay,FranceCEA,LETI,Minat
【出 处】
：
PhotonicsResearch
论文部分内容阅读
This paper reports on high-performance waveguide-integrated germanium photodiodes for optical communications applications. 200 mm wafers and production tools were used to fabricate the devices. Yields over 97% were obtained for three different compact photodiodes (10 × 10 μm and intrinsic region width of 0.5, 0.7, and 1 μm) within the same batch of three wafers. Those photodiodes exhibit low dark currents under reverse bias with median values of 74, 62, and 61 nA for intrinsic widths of 0.5, 0.7, and 1 μm, respectively, over a full wafer. Responsivities up to 0.78 A∕W at 1550 nm and zero bias were measured. Zero bias operation is possible for 25 and 40 Gbps with receiver sensitivity estimated to -13.9 and -12.3 dBm, respectively.
其他文献
浑浊介质引起的多光散射会扭曲光波传播，使图像变得模糊。浑浊透镜成像（TLI）则可以重建这种被扭曲的图像。在该方法中，需要提取输光场的复电场（复振幅）信息，以计算浑浊介质的传输矩阵。但是CCD记录的是图像的强度信息，丢失了扭曲光场的相位信息。由于物光经过浑浊介质后变成了强度剧烈变化的散斑图像，直接进行相位解调会产生较大误差。为了消除散斑强度变化的影响，分别记录扭曲光场图像、参考光图像、干涉条纹图像和背景光图像。根据对应关系换算出干涉余弦因子，对余弦因子应用希尔伯特变换进行相位解调就可以比较准确地计算出散斑的
1964年2月20日在加里福尼亚州门娄公司斯坦福研究所举行会议，讨论用作高功率光激射器泵源的闪光灯问题。会议的目的是确定目前在气休放电的特殊范围内，实验上与理论上的限制，同时也提出了往后研究和发展有效地泵浦大型光激射器系统的有希望的途径。
The original article contained a spelling error in the first author’s name. The correct name is shown here.
Noble gases (argon, krypton, and xenon) are puffed into vacuum through a nozzle to produce clusters for studying laser-cluster interactions. Good estimates of the average size of the argon, krypton and xenon clusters are made by carrying out a series of R
水体可溶性有机物(也叫黄色物质, CDOM), 直接影响水体光学特性和遥感光谱特征, 在水体生态系统、光学遥感、海洋碳循环中都发挥重要的作用。针对现有水体黄色物质(CDOM)常规测量需要对水样进行过滤等耗时耗力预处理过程, 研制了一种水体黄色物质快速测量的可用于实验室及野外分析的激光诱导荧光仪, 该仪器集成了405 nm 激光激发、高光谱接收和特征荧光光谱解析技术, 使得激光雷达能够从各种成分的叠加信号中分离和确认出特定组分。此外, 在实验室测量和分析了温度对于CDOM荧光光谱的影响, 并提出了一种荧光数
利用分步傅里叶方法，研究了PT对称介质中Airy光束的演化特性，并从截断系数、调制深度、调制宽度三个参数，研究了其对Airy光束所脱落出的孤子的传输特性的影响。研究结果发现：Airy光束在PT对称介质中传输时，在主峰位置处脱落出一个周期性变化的孤子并且孤子波形会产生一个横向位置的偏移；另外发现，截断系数a越小、调制深度P和调制因子w越大，Airy光束脱落出的孤子的峰均比越大，产生的光束干扰和光束畸变越大，阻碍光纤通信；调制深度P越小、调制因子w越大，Airy光束脱落出的孤子的峰值和峰均比出现了明显的跳跃，
采用Negativity度量两子系统间的纠缠,研究了两个全同二能级原子与腔相互作用系统中的量子纠缠。考虑原子与腔场失谐相互作用,并且原子间存在偶极相互作用的情况。利用数值计算方法,讨论了失谐量和偶极相互作用强度变化对量子纠缠的影响。研究结果表明:随失谐量增大和偶极相互作用强度增大,两原子间纠缠增强。另一方面,随失谐量逐渐增大,两原子间纠缠呈现出从不规则振荡向准周期性振荡转变。随偶极相互作用强度增大,原子间纠缠振荡频率加快。
利用溶胶凝胶法制备了双掺杂ZnO(Al,La)透明导电薄膜，在还原气氛（N2和H2的体积比为VN2VH2=964）下退火。通过X射线衍射(XRD)、紫外可见分光光度仪、扫描电镜(SEM)和双电测四探针等仪器重点考察了ZnO(Al,La)薄膜的退火温度和Al掺杂量对薄膜微观结构、表面形貌、光学性能和电学性能的影响。结果表明，随退火温度的升高，薄膜的（002）晶面择优取向生长趋势增强，平均晶粒尺寸增大，电阻率降低，透光率上升；随着Al掺杂摩尔分数的增加，晶粒尺寸减小，晶粒间间隙增多，电阻率先降低后升高。在Al
常规棱镜表面等离子体共振(SPR)传感器检测系统共振波谷浅且谷底平坦,从而导致共振波长不易确定。在常规棱镜SPR传感器系统基础上,加入偏振分光棱镜(PBS),构建了一种新型棱镜SPR传感器系统。对PBS的分光带宽展宽进行了研究,提出了基于膜系设计的展宽方法。在无水乙醇检测的实验中,滤除s偏振光后,共振波谷谷底曲率半径由86.2394减小到39.3990,近似减少为滤除s偏振光之前的1/2,这与理论