【摘 要】
:
铁基烧结制品虽然具有较高的强度,但一般需在1097—1183℃高温烧结。为了降低烧结温度,日本早稻田大学铸造研究所作了各种试验,发现在还原铁粉中添加2.5—5%wt锡—铜配比为3:
论文部分内容阅读
铁基烧结制品虽然具有较高的强度,但一般需在1097—1183℃高温烧结。为了降低烧结温度,日本早稻田大学铸造研究所作了各种试验,发现在还原铁粉中添加2.5—5%wt锡—铜配比为3:7的锡—铜合金粉或混合粉,可使铁基制品的烧结温度降至887℃左
Iron-based sintered products, although with high strength, but generally need to 1097-1183 ℃ high temperature sintering. In order to reduce the sintering temperature, the Institute of Foundry, Waseda University, Japan made various experiments and found that adding 2.5-5% tin-copper alloy powder or mixed powder with tin-copper ratio of 3: 7 in reduced iron powder can make iron Base product sintering temperature dropped to 887 ℃ left
其他文献
Using matched firm-level trade and production data over the period 2000-2006,we study the product-destination portfolio and dynamics of Chinese industrial expor
1979年以来,由于烧结厂不断改进烧结工艺和操作技术,提高了烧结矿碱度,烧结矿冶金性能有了一定程度的改善。与此同时,炼铁厂也逐步实现了烧结矿沟下过筛,不断改进筛分设备,
单剂大剂量去甲氧柔红霉素(IDA)联合大剂量阿糖胞苷(Arα-C)治疗18例(男13例。女5例,年龄20~56岁)成人急性淋巴细胞白血病(ALL)。IDA治疗前全部患者接受过Arα-C治疗。其中1
1985年12月3—5日在柳州,国家科委和中国有色金属工业总公司对国家重点攻关项目“广西大厂高铟锌精矿热酸浸出—铁矾法炼锌、萃取提铟新工艺”主流程锌的工业试验进行了鉴定
钢铁工业要持续不断地发展,就必须采用先进的技术和工艺。现代钢铁工业发展的两大课题是生产超纯净钢,要求彻底进行脱S、脱 P、脱气和大幅度简化工艺流程,向专业化、连续化
应用PAP法及ABC免疫组化法检测76例乳癌组织,结果:ER阳性占54%,PR阳性占51.3%,P53阳性占34.2%,CEA阳性占63.2%。激素受体与P53呈负相关(P<0.05),与CEA呈正相关(P<0.01),P53和CEA呈负相关(P<0.05)。3年生
1981年,公司要求把转炉炉龄提高到600炉以上,以保证炼钢生产计划的完成。为此,首先在使用耐火厂现有的焦油白云石砖的基础上,采取措施,提高炉龄。同时,对耐火厂生产的焦油白
应用LSAB法对57例乳腺癌的雌激素受体(ER)、孕激素受体(PR)和P_(53)基因表达进行研究,结果:28例ER、PR阳性组中,P_(53)阳性表达6例(20.7%);28例ER、PR阳性组中,P_(53)阳性表达
在实验室热模拟试验的基础上,本文论述在炼钢厂进行的半工业性试验的情况,比较石灰系和碳化钙系脱硫剂的脱硫能力,讨论工艺参数的影响以及估算各种脱硫剂的成本。
Based on
炼锡厂经6个月建设之后于1979年10月投产。在此以前,罗伊贝格的大部分高品位精矿出口,少部分则用传统方法在南非冶炼。低品位精矿通常出口到英国。南非锡的需求量大于本地炼