Irradiation-induced impurity segregation to grain boundaries is one of the important radiation effects on materials.For this reason, phosphorus segregation to prior austenite grain boundaries in a P-doped 2.25Cr1Mo steel subjected to neutron irradiation is examined using field emission gun scanning transmission electron microscopy (FEGSTEM) with energy dispersive X-ray microanalysis (EDX). The steel samples are irradiated around 270 and 400℃, respectively.The irradiation dose rate and dose are ～1.05×10-8 dpa/s and ～0.042 dpa respectively for 270℃ irradiation, and 1.7×10-8 dpa/s and 0.13 dpa respectively for 400℃ irradiation. The FEGSTEM results indicate that there is no apparent phosphorus segregation during 270℃ irradiation but there is some during 400℃ irradiation.