【摘 要】
：
The effects of yttrium(Y) content on precipitation hardening, elevated temperature mechanical properties and morphologies of 2519 aluminum alloy were investigat
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The effects of yttrium(Y) content on precipitation hardening, elevated temperature mechanical properties and morphologies of 2519 aluminum alloy were investigated by means of microhardness test, tensile test, optical microscopy(OM),transmission electron microscopy(TEM) and scanning electron microscopy(SEM). The results show that the tensile strength increases from 485 MPa to 490 MPa by increasing Y content from 0 to 0.10%(mass fraction) at room temperature, and from 155 MPa to 205 MPa by increasing Y content from 0 to 0.20% at 300 ℃. The high strength of 2519 aluminum alloy is attributed to the high density of fine θ precipitates and intermetallic compound AlCuY with high thermal stability. Addition of Y above 0.20% in 2519 aluminum alloy may induce the decrease in the tensile strength both at room temperature (20 ℃) and 300 ℃.
其他文献
血管内皮生长因子(vascularendothelialgrowthfactor,VEGF)是一种促血管新生因子,也具有促使血管通透性增加的作用,生长因子、炎症因子[1]、缺氧等可刺激内皮细胞、平滑肌细
Al-8.5Fe-1.3V-1.7Si alloy was prepared by spray deposition and hot extrusion. The high temperature plastic deformation behavior of the spray deposited Al-8.5Fe-
Nanocrystalline nonferrous metals (Cu, Al, and Ag) were synthesized by flow-levitation-molding method. The microstructure of the as-prepared nanocrystalline met
The electronic structure of YbB6 crystal was studied by means of density functional (GGA+U) method.The calculations were performed by FLAPW method.The high accu
The Y-Eu oxalate precursor was prepared with a homogeneous precipitation method.And the additives, Na2CO3, S, NaCl or their combination, were introduced into th
Hot plastic deformation was conducted using a new solid die on a Mg-Mn-Ce magnesium alloy. The results of microstructural examination through OM and TEM show th
With the quick development of urbanization, urban expansion has been paid more and more attention to by researchers from western countries and China. Here Wuxi
In order to investigate the effect of magnetic field on the liquid-liquid extraction, the extraction in the acetone-water-trichloroethane system was studied und
Keggin type molybdovanadophosphoric heteropoly acids,H3+nPMo12-nVnO40 (n= 1-3),were prepared by a novel environmentally benign method,and their catalytic perfor
Lanthanum phosphate was prepared in the presence of citric acid and stearic acid under methanolic conditions at pH 4.5 and pH 7, respectively.The samples obtain