【摘 要】
：
本文参照GB2358-80和GB2308-80两个试验方法标准,用多试样法对2 1/4Cr-1Mo钢的母材及其窄间隙环焊缝焊接接头的断裂韧性和金相组织进行了试验和分析。分别测定了母材和焊缝金
【机 构】
：
合肥通用机械研究所,合肥通用机械研究所,合肥通用机械研究所
论文部分内容阅读
本文参照GB2358-80和GB2308-80两个试验方法标准,用多试样法对2 1/4Cr-1Mo钢的母材及其窄间隙环焊缝焊接接头的断裂韧性和金相组织进行了试验和分析。分别测定了母材和焊缝金属、熔合线及热影响区的COD、J积分值及其显微组织。结果表明焊缝金属的断裂韧性优于母材,进行焊后热处理有助于提高母材的断裂韧性。
In this paper, with reference to GB2358-80 and GB2308-80 two test methods, the multi-sample method was used to test the fracture toughness and microstructure of the welded joints of 2 1 / 4Cr-1Mo base metal and its narrow gap Girth weld And analysis. The COD, J integral values and their microstructures of the base metal, weld metal, weld line and HAZ were measured respectively. The results show that the fracture toughness of the weld metal is better than that of the base metal. The post-weld heat treatment can improve the fracture toughness of the base metal.
其他文献
下加球化剂生产球铁和蠕铁的原理如图1所示,按下面条件实施:
The principle of producing ductile iron and vermicular iron under the nodulizer is shown in Fig. 1, and
380铝合金早在五十多年前美国即列入压铸铝合金标准,并广泛用于压铸。由于该类合金具有良好的机械性能和铸造性能,很有推广应用价值,所以英国、日本等仍在不断对其进行应用
一、前言 在一次能源载体的总储量中,煤炭资源最为丰富,约占总量的60％以上,而石油和天然气尚不足30％,油田页岩等其它燃料则在10％左右。按目前年开采能力,石油可开采20～25年,天然
薄壁内齿轮的齿表面,在高频感应加热喷水冷却淬火后,内孔多为涨大,并有时呈喇叭口、束腰、椭圆等形状。图1所示为20Cr钢制模数m3的薄壁渗碳齿轮,只要求齿部硬化为HRC58～62。
内孔单键槽的对称度测量缺乏有效的专用量具,过去采用图1所示的方法测量,既麻烦又不准确,我们制作了如图2所示的测量规,其副测头座上有固定、活功测头各一个,由螺杆调节活动
随着我国教育事业的快速发展,传统教学工作中的每一个环节都要融入创新元素。教学评价,是教学活动的重要组成部分。教学评价的方法是否合理,直接关系着学生的学习积极性,也关
赴上海采访是我许久的心愿。上海,一个早在20世纪3O年代就享有“东方巴黎”之美誉的城市,在前不久胜利闭幕的APEC会议上,又向全国全世界人民展示了她的高度的城市管理水平及
激光表面热处理包括退火、相变硬化、合金化、上光、包覆、细晶化、冲击淬火等,目前最实用的是相变硬化工艺。相变硬化工艺在应用上有其独特优点,其工艺控制技术包括聚焦方式
全省人大宜传暨报刊发行工作会议于9月4日在汉川县召开。各市、州、直管市和部分县人大常委会办公室、代表工作委员会、地区人大联络组负责人欢聚一堂,共同商议1997年度宜传
“文革”期间,许多深受广大群众喜爱的文艺作品饱受摧残,许多优秀的文艺工作者遭到迫害。1976年10月粉碎“四人帮”以后,这些文艺作品才得以重见天日。空政文工团的民族歌剧《江姐》,因为江青的否定和打压,被封存长达12年之久,直到1977年春天才开始第二次排演。此时的空政文工团演员和创作人员在“文革”期间走的走,散的散,所剩无几。加上极左思潮的影响也难以彻底消除,还时时在困扰着文艺工作者。因此,当《江