Electroluminescence (EL) is observed from the Au/Si-rich SiO2 film/p-Si diodes, in which the Si-rich SiO2 films are scored deliberately by a diamond tip. The EL intensity of the scored diode annealed at 800°C is about 6times of that of the unscored counterpart. The EL spectrum of the unscored diode could be decomposed into two Gaussian luminescence bands with peaks at about 1.83 and 2.23 eV, while for the EL spectrum of the scored diode, an additional Gaussian band at about 3.0eV appears, and the 1.83-eV peak increases significantly in intensity. The photoluminescence (PL) spectrum of an unscored Si-rich SiO2 film has only one band peaking at about 1.48eV, whereas the PL spectrum of the scored one has two bands at about 1.48 and 1.97eV. We consider that the high-density defect regions produced by the scoring provide new luminescence centres and become some types of nonradiative centres in the Si oxide layer, which thus result in changes of the EL and PL spectra.