Cold-rolled 2024–T3 sheet alloy was subjected to bobbin-tool friction stir welding(BTFSW). The microstructural characteristics and mechanical properties of the nugget zone in the as-welded state were investigated. The results show that the equiaxed grain size of BTFSW 2024–T3 alloy decreases from 7.6 to 2.8 μm as the welding speed is increased from 80 to 120 mm/min; in addition,fine grains are generated in the nugget zone and the size distribution is non-uniform. All Al_2 Cu Mg(S′) precipitates dissolve into the Al matrix,whereas Mn-rich phases confirmed as T phases(Al_(20)Cu_2Mn_3,Al_6 Mn,or Al_3Mn) remain unchanged. The optimized parameters for BTFSW are verified as the rotation speed of 350 r/min and the travel speed of 100 mm/min. The variations in precipitation and dislocation play more important roles than grain size in the nugget zone with respect to influencing the mechanical properties during the BTFSW process. After the BTFSW process,the fracture mode of base material 2024–T3 alloy transforms from ductile rupture to ductile-brittle mixed fracture. Cold-rolled 2024-T3 sheet alloy was subjected to bobbin-tool friction stir welding (BTFSW). The microstructural characteristics and mechanical properties of the nugget zone in the as-welded state were. The results show that the equiaxed grain size of BTFSW 2024-T3 alloy decreases from 7.6 to 2.8 μm as the welding speed is increased from 80 to 120 mm / min; in addition, fine grains are generated in the nugget zone and the size distribution is non-uniform. All Al 2 Cu Mg (S ’) Precipitates dissolve into the Al matrix, while Mn-rich phases confirmed as T phases (Al_ (20) Cu_2Mn_3, Al_6Mn, or Al_3Mn) remain unchanged. The optimized parameters for BTFSW are verified as the rotation speed of 350 r / min and the travel speed of 100 mm / min. The variations in precipitation and dislocation play more important roles than grain size in the nugget zone with respect to influencing the mechanical properties during the BTFSW process. After the BTFSW process, the fracture mode of base material2024-T3 alloy transforms from ductile rupture to ductile-brittle mixed fracture.