【摘 要】
：
采用性能测试、金相观察、扫描电镜及能谱测定等方对断裂叶片进行了分析。结果表明,叶片材质正常,但在酸性介质的作用下叶片表面及内部产生了大量腐蚀坑,在循环应力的作用下
【机 构】
：
四川大学制造科学与工程学院,成都成发科能动力工程有限公司,
论文部分内容阅读
采用性能测试、金相观察、扫描电镜及能谱测定等方对断裂叶片进行了分析。结果表明,叶片材质正常,但在酸性介质的作用下叶片表面及内部产生了大量腐蚀坑,在循环应力的作用下腐蚀坑成为裂纹源,形成裂纹并不断长大和扩展,最终导致整个叶片疲劳失效断裂。
Fracture blades were analyzed by performance test, metallographic observation, scanning electron microscopy and energy spectrum measurement. The results showed that the leaf material was normal, but a large number of corrosion pits were formed on the surface and inside the blade under the action of acidic medium. The corrosion pits became the source of cracks under the action of cyclic stress. The cracks formed and grew and expanded eventually leading to fatigue failure of the entire blade fracture.
其他文献
Bobby was getting cold sitting out in his back yard in the snow.He didn’t wear boots.He didn’t like them and anyway he didn’t own any.The thin sneakers he wo
针对当前工控系统的体积大、成本高、不稳定等缺点,提出基于单片机ARM嵌入式技术开发设计出一款成本低、性能稳定的机床数控系统。该系统由单片机ARM和运动控制卡为硬件控制
自Ｇｏｄａ于１９７０年提出谱峰度参量Ｑｐ以来，迄今表征波群强度的因子己有十多种。对文中提及的较常用的１１种因子即以后被称为现有波群因子，各作者都强调自己的优点，但何者为较好，直至目前尚无客观的
斗转星移,人类已迈进了充满希望与激情的21世纪.在这世纪之初,高新技术产业对世界经济已产生巨大影响.两年多来,在上级政府及有关部门的领导与支持下,我们东辰集团解放思想,
职业自主权的概念是指我们每个人应对自己的事业负责.人到中年,职业变动恰是我们成为拥有"自己的”事业的企业家的大好时机,而事业的开创须借助你的洞察力与想象力,并最大限
俄勒冈大陆边缘上的气体水合物胡安·德富卡板块在美国西北部和加拿大西南部的滨海以约４．５ｃｍ／ａ的速率向北美板块下倾斜俯冲。如今，俯冲板块上的大部分含有大量砂质、粉砂质浊积岩的沉
—In the designing of the flexible fender pile,M-method is usually adopted.But M-method isusable only in the case that the value of the force(moment M and shear
本文主要分析进口燃油锅炉的运行,研究管理的模式,解决管理问题。
This article mainly analyzes the operation of imported oil-fired boilers, studies the management m
教学过程Step 1.Flash复习学生所学的动词词组设计意图:课前滚动出现,吸引其注意力,为学生有话可说作铺垫。Step 2.Warming upT:Hello,boys and girls.I’myour teacher.My f
国家高技术研究发展计划成果产业化荣成基地建设进展顺利 荣成市是国家科技部首批公布的“863”计划成果产业化基地之一,也是全国唯一的一个海洋”863”计划成果产业化基地