In this study, Al-Zn and Al-Mg coatings were deposited on steel substrates by an arc thermal spray process. X-ray diffraction and scanning electron microscopy were used to characterize the deposited coatings and corrosion products. Open circuit potential
【机 构】
：
Department of Architectural Engineering, Hanyang University, 1271 Sa 3-dong, Sangrok-gu, Ansan 15588
论文部分内容阅读
In this study, Al-Zn and Al-Mg coatings were deposited on steel substrates by an arc thermal spray process. X-ray diffraction and scanning electron microscopy were used to characterize the deposited coatings and corrosion products. Open circuit potential (OCP), electrochemical impedance spectroscopy, and potentiodynamic studies were used to assess the corrosion characteristics of these coatings after exposure according to the Society of Automotive Engineers (SAE) J2334 solution of varying durations. This solution simulates an industrial environment and contains chloride and carbonate ions that induce corrosion of the deposited coatings. However, the Al-Mg alloy coating maintained an OCP of approximately-0.911 V versus Ag/AgCl in the SAE J2334 solution even after 792 h of exposure. This indicates that it protects the steel sacrificially, whereas the Al-Zn coating provides only barrier-type protection through the deposition of corrosion products. The Al-Mg coating acts as a self-healing coating and provides protection by forming Mg6Al2(OH)16CO3 (Al-Mg layered double hydroxides). Mg6Al2(OH)16CO3 has interlocking characteristics with a morphology of plate-like nanostructures and an ion-exchange ability that can improve the corrosion resistance properties of the coating. The presence of Zn in the corrosion products of the Al-Zn coating allows dissolution, but, at the same time, Zn5(OH)6(CO3)2 and Zn6Al2(OH)16CO3 are formed and act to reduce the corrosion rate.
其他文献
The hot deformation behavior of Fe-26Mn-6.2Al-0.05C steel was studied by experimental hot compression tests in the temperature range of 800-1050 ℃ and strain rate range of 0.01-30 s-1 on a Gleeble-3500 thermal simulation machine.The microstructural evolut
In this work,the corrosion behaviours of the amorphous Ni84.9Cr7.4Si4.2Fe3.5 alloy and its crystalline counterpart are studied in acidic,neutral,and alkaline solutions by scanning electron microscopy,electrochemical impedance spectroscopy,and potentiodyna
Anisotropic SmCo5/Co nanocomposite powders have been prepared by electroless Co deposition on commercial SmCo5 powders with hydrazine as reducer.The Co particles are mainly in the range of 8-27 nm and form dense/continuous soft magnetic coatings on the su
The effects of ausforming procedure and subsequent annealing treatments on microstructures of cobalt (Co) samples are investigated by electron channeling contrast and electron backscatter diffraction techniques.Results show that the ausformed Co samples c
Hybrid aluminum matrix composite powders reinforced with bimodal-sized Al2O3 particles were synthesized by mechanical milling.Two different approaches were investigated for the addition of submicron-and nano-sized Al2O3 particles to the aluminum powders.I
Hot compression tests were carried out with specimens of 20Cr-24Ni-6Mo super-austenitic stainless steel at strain rate from 0.01 to 10 s-1 in the temperature range from 950 to 1150 ℃,and flow behavior was analyzed.Microstructure analysis indicated that dy
In this work,surface characterization and electrochemical measurement were employed to investigate the effects of magnetic field (MF) on the corrosion of Q235 carbon steel in a NaCl solution containing sulphate-reducing bacteria (SRB) or extracellular pol
The hot deformation behavior of a medium-Mn steel was studied in terms of hot compression flow curves in the temperature range of 850-1050 ℃ and strain rates of 0.05-10 s-1.The thermo-mechanical analysis was carried out and suggested that the microstructu
Corrosion inhibition of tolytriazole for galvanized steel was studied in 5 mM NaCl by using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS),scanning vibrating electrode technique (SVET).The results of EIS and polarization tes
In this work, a series of biodegradable pure iron, Fe-30Mn and Fe-30Mn-Ag alloys were developed by using a rapid solidification technology. A fine α-Fe dendrite was formed in pure iron, resulting in a high compressive yield strength of above 300 MPa. The