The supported membranes of Al2O3 and its modification membranes were prepared.Al2O3,Al2O3-SiO2-TiO2 and Al2O3-SiO2-TiO2-ZrO2 membranes were mamufatured by the s
论文部分内容阅读
The supported membranes of Al2O3 and its modification membranes were prepared.Al2O3,Al2O3-SiO2-TiO2 and Al2O3-SiO2-TiO2-ZrO2 membranes were mamufatured by the slip-casting process using mixing boehmite,silicate,titania and zirconia sols under proper conditions,then the composite membrane was prepared.The structure and characteristics of the membrane were determined by XRD,SEM and AFM measurement.The conditions of preparation of the membrane are discussed.The thickness of the layer is about 1-2μm,the diameter of an average pore is 200-300nm and has a narrow pore distribution without crack forming.By changing the ratios of Al∶Si∶Ti∶Zr(mol),variations of surface pore size of Al2O3-SiO2-TiO2-ZrO2 membrane can be gained.
其他文献
Pre-dispersed solvent extraction (PDSE) was used to extract quercentin from its diluted solution. Theinfluences of temperature, phase volume ratio (PVR), concen
The microstructure of gibbsite precipitated with seeds from sodium aluminate solution was studied using SEM. The results show that there are a lot of fine secon
Al2O3/Al composite was fabricated by the reaction between SiO2 and molten aluminum.The microstructures of the composite obtained under different reaction condit
Two anode catalysts with Pt, MoS2 and composite metal sulfides (MoS2+NiS), are investigated forelectrochemical oxidation of hydrogen sulfide in solid oxide fuel
A way of manufacturing nickel material with fractal structure has been studied. Some algae with natural fractalstructure were used as the basic substrates. The
Experiments of biomass pyrolysis were carried out in a fluidized bed, and dynamic signals of pressure andtemperature were recorded. Correlation dimension was em
Large-quantity growth of ZnO nanorods is achieved by oxidation of Zn powders with catalyst-free method.The products are characterized using X-ray diffraction,sc
Raman lasers based on potassium gadolinium tungstate and lead tungstate crystals pumped by a≈120 ps Nd: YAG laser at 1.064 μm were developed. High reflection
A method named as "volume-expanding and pressure-reducing adsorption" is proposed. It can be usedto measure the isotherms under supercritical condition. The ads