Hydration heat behavior and kinetics of blended cement containing up to 20％ MSWI fly ash were investigated based on its hydration heat evolution rate measured by isothermal calorimeter. Kinetics parameters, N and K, and hydration degree, Ca(OH)2 content,
【机 构】
：
School of Environment and Architecture, University of Shanghai for Science and Technology, Shanghai
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Hydration heat behavior and kinetics of blended cement containing up to 20％ MSWI fly ash were investigated based on its hydration heat evolution rate measured by isothermal calorimeter. Kinetics parameters, N and K, and hydration degree, Ca(OH)2 content, were also calculated and analyzed. According to the experimental results, the induction period was elongated, the second heat evolution peak was in advance, and the third hydration heat peak could be detected due to MSWI fly ash pozzolanic reaction. The hydration reaction rate was controlled by nucleation kinetics in the acceleration period and then by diffusion in the decay period, but in the deceleration period, the hydration experienced a dual controlling reaction of autocatalytic chemical reaction and diffusion. The hydration rate of blended cement was faster. Ca(OH)2 content increased before 14 days.
其他文献
The pastes containing different dosages of fly ash were taken into ultraviolet radiation and low temperature freeze condition simultaneously(URL) for 30 days and only ultraviolet radiation condition(UR) for 30 days after standard curing,so as to investiga
Taking dodecanethiol as the representative, we investigated the corrosion inhibition perfor-mance of SAL in seawater under pressures from 0.1 to 9 MPa. By using scanning Kelvin probe, the dodeca-nethiol SAL is confirmed to build on Cu surface, and the mod
To develop an efficient and bio-compatible way to improve the thermal and mechanical properties of addition type liquid silicone rubber (LSR),a series of modified LSR samples were prepared by introducing octavinyl-polyhedral oligosilsesquioxanes (VPOSS) a
To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstructure evolutions were systematically
A new type of capric acid (CA)-acid expanded vermiculite (AEV) composite phase change material (PCM) with improved adsorption ability and interface adhesive strength was developed. Through the analysis of non-isothermal phase transition kinetics, modified
The isothermal absorption properties and kinetic model of Cr (Ⅵ) and Cr (Ⅲ) onto ettringite were investigated using the batch adsorption method. IR analysis was used to study the difference and mechanism of the adsorption of chromium ions with different v
The mechanical and thermal properties of steel reinforced concrete columns with CFRP reinforcement were examined after exposure to a high temperature of 500℃. The concrete made with normal and recycled coarse aggregate (RCA) was fabricated and three diffe
Due to the intrinsic nature of a heterogeneous and anisotropic microstructure of cement based materials and the small indentation size, the measured microhardness values are subject to considerable variability. This work presents an in-depth assessment of
Cement raw meal with MSS and different heavy metals was blended to examine the fixation ratios, chemical species, and cement crystalline phases in clinkers. The results showed that blending MSS could decrease the fixation ratio of Cr, Ni, Cu, and Zn in th