【摘 要】
:
本文对缝管技术进行了详细研究。缝管富集是一种在管内浓集待测元素原子的方法,它较原子捕集更简单易行,灵敏度较常规方法提高2—8倍。通过实验选择了最佳条件,对银矿样中共
【机 构】
:
吉林大学化学系,吉林大学化学系,吉林大学化学系,吉林大学化学系 87届毕业生
论文部分内容阅读
本文对缝管技术进行了详细研究。缝管富集是一种在管内浓集待测元素原子的方法,它较原子捕集更简单易行,灵敏度较常规方法提高2—8倍。通过实验选择了最佳条件,对银矿样中共存元素进行了干扰研究,并在最佳条件下对一批银矿样进行了分析测定。方法的回收率为95—115%,相对标准偏差为4.4%。
In this paper, the seam pipe technology has been studied in detail. Seamless tube enrichment is a method of concentrating the atoms of the elements to be tested in the tube. It is easier and more sensitive than atomic capture and improves the sensitivity by 2-8 times as compared with conventional methods. The optimal conditions were selected through experiments, and the co-existing elements in the silver ore sample were studied for interference. Under the optimal conditions, a batch of silver samples were analyzed and determined. The recovery was 95-115% with a relative standard deviation of 4.4%.
其他文献
用360MHz和250MHz超导核磁共振波谱仪测定了可待因(codeine)的~(13)C核弛豫参数。研究了分子稳定运动状态。用我们提出的理论模型分析了实验结果。计算了分子绕R_1、R_2、R_3
以前未成立民主理财小组,财务不公开,群众对村里财务是“雾里看花”,现在村级财务实行民主理财和“两公开”后,在湖北武穴农村出现了不少新故事。四怒汉公开栏前怒气消去年6月间,在
本文报道了仲胺醇 N2125萃取与反萃取 Tl(Ⅲ)的性能研究,并用饱和法与等摩尔系列法测定萃合物的组成为(N2125)HTlCl_4,通过红外光谱与核磁共振谱探讨了萃取 Tl(Ⅲ)的机理为离
地学资源成为旅游资源、并经过开发成为旅游产品吸引人前往,其中隐含着美学价值的发现与实现;地学旅游资源美学价值的发掘对于资源开发利用的效果乃至成败不是可有可无的而是
在ICP-AES分析时,试液成雾粒后,经过雾室,其细雾粒由氩气载入等离子区,而95%以上的大雾粒没有利用而作废液被排出。当可得到的样品量或试液不受限制时,这并没有多大影响。随
本文主要研究不同含量的钴、硫酸以及硫酸钴对测定镁的影响。随着钴、硫酸和硫酸钴含量的增加,镁的吸光度下降。实验证明加入一定量的硝酸镧和氯化锶都不能消除这种干扰。经
本文发现萃取色层法分离铜中的金.用 P_(350)为固定相、硅胶为担体,以盐酸和亚硫酸钠溶液为流动相,用盐酸淋洗下铜后,改用亚硫酸钠溶液淋洗金.测定结果良好,回收率在90~105%之
本文用三角波动电位扫描法对活性炭表面电化学性质进行了探讨.测得活性炭表面基团的浓度为3.4×1~(-7)(moles/em~2),表面基团数为1.08×1~(20),接近文献值.确定表面电活性基
铅印本就是采用现代铅印技术排印的书籍。这种印本,开始出现于清朝末年。清道光二十三年(1843年),在当时的上海成立了我国第一个铅印出版机构——墨海书馆,于咸丰七年(1857年
本文报道了Ba-Nd-Cu-O体系中,样品组成热处理条件对其相组成和超导电性的影响。制得一系列液氮温区超导体,最高Tc(ρ=0)为84.5K。通过对其物相组成和超导电性关系研究,表明Ba