【摘 要】
：
The CaCu3Ti4O12 (CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process (synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and electrical properties were investiga
【机 构】
：
State Key Laboratory for Environment- friendly Energy Materials, Southwest University of Science and
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The CaCu3Ti4O12 (CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process (synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and electrical properties were investigated. The phase composition was determined by X-ray diffraction and the microstructure was examined by SEM. The dielectric constant, dielectric loss, and resistance of the ceramic were also determined by a precision impedance tester. The results show that, as the synthesis temperature increases, the CCTO ceramic grain size decreases and the stoichiometric ratio of Cu/Ca at the grain boundary increases, the dielectric constant increases and the dielectric loss decreases (40 < f < 10 kHz). In addition, when the synthesis time is shorter than 12 h, the Cu/Ca ratio of CCTO decreases and the dielectric constant increases with time increase. However, when the synthesis time exceeds 12 h, this trend is just the opposite. It is further proved that Cu at the grain boundary is not conducive to the dielectric constant of CCTO.
其他文献
SnO2/AgIO4 hybrids were fabricated by an in-situ synthetic method at room temperature. The structure, morphology, light response range, separation efficiency of the electron-hole pairs and elements of the as-synthesized samples were characterized by adopt
The effects of surface adsorption of bovine serum albumin (BSA) and human gamma-globulin (HGG) on the tribological performance of a DLC film were investigated using a quartz crystal microbalance with dissipation (QCM-D), a ball-on-disk reciprocating tribo
High-quality LDH-SO4-CO3 whiskers were synthesized via liquid precipitation method using MgSO4·7H2O and Al2(SO4)3·18H2O as precursors and Na2CO3-NaHCO3 buffer solution as precipitant. The influence of buffer solution concentration on the characteristics o
Al foam sandwich panel (AFS) with metallic bonding was fabricated by foaming a hot-pressed three-layer composite with two steel facesheets and a melt route precursor as core. The melt route precursor was fabricated by dispersing undecomposed blowing agent
To improve the weak corrosion resistance of silicon steel to acid solution and alkaline solution with high temperature, a stable hierarchical micro/nanostructure superhydrophobic surface with myriad irregular micro-scale hump and sheet-like nanostructure
Optimizing highly porous fibrous ceramics, like bird\'s nest structure, were obtained by vacuum impregnation method with mullite fibers and alumina sol as raw material. The influences of impregnation cycles on the property of the sample, such as porosit
A novel method to prepare an electrocatalyst with a new structure and high catalytic performance was reported. Two-dimensional (2D) PtRu nanoclusters have been successfully deposited on graphene oxide and carbon black supports. Compared with the commercia
Five types of KNO3-NH4VO3-rare earth metal nitrate (K-V-rare earth metal) catalysts supported on α-porous alumina ceramic substrates were prepared by a coating method. All the catalysts were characterized by X-ray diffraction and thermogravimetry/differen
In order to improve the efficiency of β-CD, the inclusion complex of β-CD and resorcinol bisdiphenylphosphate (RDP) (β-CD@RDP) was prepared, which β-CD was as the host component and RDP was as the guest. The structure and thermal stability property of β-C
The p-type Ge doped Fe0.4Co3.6Sb12-xGex skutterudites with multi-scaled impurity dots (500 nm-2 mm) were successfully prepared by using melt-quenching (MQ) and subsequent spark plasma sintering (SPS) technique. Compared with traditional method, the new te