【摘 要】
:
Spinel lithium manganese oxide cathode materials were synthesized using the ultrasonic-assisted sol-gel method.The synthesized samples were investigated by diff
【机 构】
:
School of Chemistry and Chemical Engineering,Department of applied Chemistry
论文部分内容阅读
Spinel lithium manganese oxide cathode materials were synthesized using the ultrasonic-assisted sol-gel method.The synthesized samples were investigated by differential thermal analysis (DTA) and thermogravimetry (TG),powder X-ray diffraction (XRD),scanning electron microscopy (SEM),cyclic voltammetry (CV),and the charge-discharge test.TG-DTA shows that significant mass loss occurs in two temperature regions during the synthesis of LiLa0.01Mn1.99O3.99F0.01.XRD data indicate that all samples exhibit the same pure spinel phase,and LiLa0.01Mn1.99O3.99F0.01 and LiLa0.01Mn1.99O4 samples have a better crystallinity than LiMn2O4. SEM images indicate that LiLa0.01Mn1.99O3.99F0.01 has a slightly smaller particle size and a more regular morphology structure with narrow size distribution.The charge-discharge test reveals that the initial capacities of LiMn2O4,LiLa0.01Mn1.99O4,and LiLa0.01Mn1.99O3.99F0.01 are 130,123,and 126 mAh·g-1,respectively,and the capacity retention rates of the initial value,after 50 cycles,are 84.8%,92.3%,and 92.1%,respectively.The electrode coulomb efficiency and CV reveal that the electrode synthesized by the ultrasonic-assistexi sol-gel (UASG) method has a better reversibility than the electrode synthesized by the sol-gel method.
其他文献
The hot deformation behaviors of GCr15 bearing steel were investigated by isothermal compression tests, performed on a Gleeble-3800 thermal-mechanical simulator
Zirconia powders doped with yttrium prepared by special liquid-phase precipitation method were sintered by spark plasma sintering (SPS) to obtain high performan
The annealing condition,Al content,and field amplitude dependences of the complex permeability for Nb-poor Finemet type alloys,Fe73.5Si13.5B9Cu1Nb3-xAlx (x=0,0.
To investigate the influence of stress alone on the stray field signals of ferromagnetic materials, the static tensile tests of 0.45%C steel and 45CrNiMoVA stee
A kind of networked control system is studied; the networked control system with noise disturbance is modeled based on information scheduling and control co-des
Fe/Gd multilayers were prepared by alternate vapor deposition of pure Fe and Gd at a rate of 0.01-0.03 nm/s in an ultra-high-vacuum electron-gun evaporation sys
The driving voltage and current signals of piezoeeramie transducer (PZT) were measured directly by designing circuits from ultrasonic generator and using a data
The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size,reaction temperature and the sum concent
The platinum nanoparticles supported on self-organized TiO2 nanotubes (Pt-TiO2/Ti) were prepared using electrochemical anodic oxidation followed by cathodic red
根据实际情况,把天津地区划分为5个地区单元,通过现场采样及室内分析测试,研究了各单元表层土壤多环芳烃的分区特征.结果表明,在划分的5个单元区中,PAHs总浓度及各组分浓度基