【摘 要】
：
Highly porous nitrogen-doped carbon materials were synthesized by the carbonization of a low-cost porous covalent triazine polymer,PCTP-3,which had been synthesized by the AlCl3 catalyzed FriedelCrafts reaction of readily available monomers.The nature of
【机 构】
：
Department of Chemistry and Chemical Engineering, Inha University, Incheon 402-751, South Korea
论文部分内容阅读
Highly porous nitrogen-doped carbon materials were synthesized by the carbonization of a low-cost porous covalent triazine polymer,PCTP-3,which had been synthesized by the AlCl3 catalyzed FriedelCrafts reaction of readily available monomers.The nature of the bond and structure of the resulting materials were confirmed using various spectroscopic methods,and the effects of KOH activation on the textural properties of the porous carbon materials were also examined.The KOH-activated porous carbon (aPCTP-3c) materials possessed a high surface area of 2271 m2 g 1 and large micro/total pore volumes of 0.87/0.95 cm3 g-1,respectively,with narrower micropore size distributions than the porous carbon prepared without activation (PCTP-3c).The aPCTP-3c exhibited the best CO2 uptakes of 284.5 and 162.3mgg 1 and CH4 uptakes of 39.6 and 25.9mgg-1 at 273 and 298K/1 bar,respectively,which are comparable to the performance of some benchmark carbon materials under the same conditions.The prepared materials exhibited high CO2/N2 selectivity and could be regenerated easily.
其他文献
Self-discharge is a significant issue in electric double layer energy storage,which leads to a rapid voltage drop and low energy efficiency.Here,we attempt to solve this problem by changing the structure of the electric double layer into a de-solvated sta
A free-standing paper-like three-dimensional graphene framework (3DGF) with orientated laminar structure and interconnected macropores,was obtained by the hard template-directed ordered assembly.As the sacrificial templates,polystyrene (PS) latex spheres
MoS2 is a promising anode material for sodium ion batteries owing to its two-dimensional layered structure and high specific capacity.But it still exhibits a poor cycle stability and limited rate capability for Na storage because of its poor electrical co
Aluminum-ion batteries (AIBs) are attracting great attentions recently because of the high volumetric capacity,natural abundance of Al and operational safety.Using metallic Al as anode,the development of suitable cathode materials is a key issue to build
N-doped coaxial CNTs@α-Fe2O3@C nanofibers have been successfully synthesized according to a facile solvothermal/hydrothermal method.The obtained CNTs@α-Fe2O3@C nanofibers composites exhibited special three-dimensional (3-D) network structure,which endows
Use of metallic Li anode raises serious concerns on the safety and operational performance of Li-S batteries due to uncontrolled hazard of Li dendrite formation,which is difficultly eliminated as long as the metallic Li exists in the cells.Pairing lithium
Fe3-xO4 raspberry shaped nanostructures/graphene nanocomposites were synthesized by a one-step polyol-solvothermal method to be tested as electrode materials for Li-ion battery (LIB).Indeed,Fe3-xO4raspberry shaped nanostructures consist of original orient
V-doped SBA-16 catalysts (V-SBA-16) with 3D nanocage mesopores have been successfully synthesized by a modified one-pot method under weak acid condition.The obtained materials were characterized by means of small angle XRD,N2 adsorption-desorption,TEM,UV-
The Ni2P/MgAlO catalysts with different MgO/Al2O3 ratios were prepared by the phosphidation of corresponding Ni/MgAlO catalysts with triphenylphosphine in liquid phase.It was found that the MgO/Al2O3 ratio affected the Ni2P/MgAlO catalysts significantly.T
CO2 capture with ionic liquids (ILs) has attracted many attentions,and most works focused on absorption ability at ambient temperatures,while seldom research was concerned at elevated temperatures.This not only limits the CO2 absorption application at ele