Microstructural evolution of Au-Sn solder prepared by laminate rolling during annealing process

来源 :Rare Metals | 被引量 : 0次 | 上传用户:orc2008
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The microstructural evolution and interfacial reaction of the Au/Sn/Au/Sn/Au/Sn/Au couples were investigated during annealing at 453,523,and 543 K for up to 240 h.The Au/Sn combination formed a rapid diffusion system.Even in rolled Au-Sn solder,three phases,such as AuSn,AuSn2,and AuSn4,were formed.After initial annealing at 453 K,the diffusion layers of AuSn,AuSn2,and AuSn4,which were formed after rolling,expanded gradually and then fully transformed into ζ phase(containing Sn from 10% to 18.5%,mole fraction) and δ(AuSn) phase.As a whole,the microstructure of the couple was stable during annealing at 453 K.The solid-state interfacial reaction was much faster at 523 K than at 453 K.After annealing at 523 K for 6 h,the AuSn,AuSn2,and AuSn4 were fully transformed into the ζ phase and δ phase(AuSn) .In spite of the prolonged annealing time for up to 240 h,no significant change of the interfacial microstructure occurred,and the microstructure of the couple was stable during annealing at 523 K.When annealing at 543 K,however,the interfacial of Au/Sn was transformed into solid-liquid state,and the whole couple formed a eutectic structure rapidly,causing the solder to be brittle.The study results clearly demonstrate that the service temperature of the Au-Sn solder should be lower than 543 K. The microstructural evolution and interfacial reaction of the Au / Sn / Au / Sn / Au / Sn / Au couples were investigated during annealing at 453,523, and 543 K for up to 240 h. The Au / Sn combination formed a rapid diffusion system. Even in three times, such as AuSn, AuSn2, and AuSn4, were formed. After initial annealing at 453 K, the diffusion layers of AuSn, AuSn2, and AuSn4, which were formed after rolling, expanded gradually and then fully transformed into ζ phase (containing Sn from 10% to 18.5%, mole fraction) and δ (AuSn) phase. As a whole, the microstructure of the couple was stable during annealing at 453 K. The solid-state interfacial reaction was much faster at 523 K than at 453 K. After annealing at 523 K for 6 h, the AuSn, AuSn2, and AuSn4 were fully transformed into the ζ phase and δ phase (AuSn). In spite of the prolonged annealing time for up to 240 h, no significant change of the interfacial microstructure occurred, and the microstructure of the couple was stable during annealing at 523 K.When annealing at 543 K, however, the interfacial of Au / Sn was transformed into solid-liquid state, and the whole couple formed a eutectic structure rapidly, causing the solder to be brittle. The study results clearly demonstrate that the service temperature of the Au-Sn solder should be lower than 543 K.
其他文献
随着新课改的不断深入和改革,传统的小学数学教学模式已经不能满足教育发展的需求,因此,在实际的小学数学教学中,应该将生活化教学融入课堂教学中,进而不断地挖掘学生的数学
期刊
自1998年11月至1999年5月,对我院妇科慢性盆腔炎病人100例进行了中西医结合治疗,效果显著,治疗组显效率87%,总有效率96%,对照组显效率40%,总有效率为72.5%,治疗组显效率及总有效
高中英语难学,恐怕是相当一部分高中学生的观点,那高中英语为什么难学呢?仅仅因为需要记忆就使得那么多学生害怕英语学习吗?这些问题往往只是表面现象,真正的解决方法需要结
1994年,汪民进入公安部第一研究所计量室工作,并从计量员干起。2000年12月汪民成为神盾计量校准中心副主任。2012年10月起,她一直在公安部安全与警用电子产品质量检测中心神
20世纪90年代中期,黄健翔在中央电视台体育频道一露面,就不同寻常。他以自己独特的主持风格赢得了同行和观众特别是广大球迷的认同。黄健翔是从一个普通的球迷一跃成为著名
我院自1992年至1995年,应用中西医结合治疗结核性渗出性胸膜炎87例,并与单纯西药治疗对照组52例比较,相对疗效较好。fiB床资料139例均为同期住院病人,其中男88例,女51例;年龄11~71岁
不孕症属妇科常见病,疑难病证,单一治疗疗效差,对输卵管阻塞性不孕症作者用六联疗法综合系统治疗65例,结果妊娠52例,无效13例,总有效率80%,提示对阻塞性不孕症的治疗,应中西医
患者,男,31岁,干部,病历号91182。因心悸气短发热,左上腹肿块2月余,于1991年1月28日入院。体检:T385℃,P104次/min,Bp83/60mmHg,两肺散在湿性罗音,胸骨下段轻度压痛,心脏(-),皮肤及巩膜
一头浓密的短发,间或有少许白丝;轮廓分明的脸庞,透着黑红的肤色;中气十足的嗓门,说话干脆利落,一双睿智的目光,在眼镜片后闪动……年已74岁的崔家龙,给人的印象就像50多岁的
从事教育工作多年,一直有一个问题也是遗憾困扰着自己,常常使自己辗转反侧.就是所谓“差生”的存在.