【摘 要】
:
在MgO(100)基片上利用脉冲激光沉积技术制备了掺有Ag纳米颗粒的BaTiO3复合薄膜.通过X射线衍射对薄膜的结构进行了表征,利用透射电子显微镜对Ag纳米颗粒的尺寸、形态进行了观
【机 构】
:
华中科技大学光电子科学与工程学院,中国科学院物理研究所 武汉430074中国科学院物理研究所,北京100080,北京100080
论文部分内容阅读
在MgO(100)基片上利用脉冲激光沉积技术制备了掺有Ag纳米颗粒的BaTiO3复合薄膜.通过X射线衍射对薄膜的结构进行了表征,利用透射电子显微镜对Ag纳米颗粒的尺寸、形态进行了观测,X射线光电子能谱结果表明Ag呈金属态.在410—500nm范围内观测到了Ag纳米颗粒引起的等离子振荡峰,随着后处理温度和Ag颗粒浓度的增加,吸收峰发生红移,并出现了双峰现象.
The BaTiO3 composite films doped with Ag nanoparticles were prepared by pulsed laser deposition on MgO (100) substrate.The structure of the films was characterized by X-ray diffraction and the size and morphology of the Ag nanoparticles were characterized by transmission electron microscopy The results of X-ray photoelectron spectroscopy showed that Ag was in metallic state, and the peak of plasma oscillation induced by Ag nanoparticles was observed in the range of 410-500 nm. The absorption peak shifted red with the increase of post-treatment temperature and concentration of Ag particles. Bimodal phenomenon appeared.
其他文献
园林绿化工程是建设风景园林绿地的工程,为保证景观绿化工程施工能满足要求,确保工程质量,本文尝试着提出园林绿化施工中一些规范性的技术原则、要求以及道路绿化需注意的事
园林绿化在城市发张中日益受到重视,环境植物保护的任务也越来越艰巨,维护生态平衡、增强生物间的协调共存是植树造林、园林绿化的根本宗旨.本文分析了园林植物保护现状,并提
目的探讨原癌基因pokemon在胶质瘤中的表达水平。方法分别使用Real-time PCR和western blot技术检测胶质瘤(22例)和正常脑组织(22例)中pokemon的RNA水平和蛋白水平。结果胶质
许多不同类型的植物种子存在休眠现象,可通过层积处理、生长物质处理以及化学药剂处理等方法来解除种子休眠,本文就不同类型植物种子休眠解除方法进行概述,以期有助于农业生
生态经济林是针对干旱瘠薄森林覆盖率低、水土流失严重,土地生产力低的现状,结合当前国家生态环境建设综合治理项目而提出来的,属于生态林业的范畴.它是以自然规律和经济规律
目的:筛选复方颗粒剂中总多糖的最佳提取工艺。方法:以总多糖提取率及浸膏得率为综合指标,采用正交试验对复方桑黄颗粒中总多糖的水提取工艺进行优选。结果:最佳提取工艺为:
该文提出了一种适合空时网格码的联合迭代最大似然估计和译码的方法,利用较少的导频,能够获得比传统非迭代最大似然译码更好的系统性能,仿真结果显示经过4次迭代,其性能与接
为了对颜色视觉匹配中的明度阈值特性进行评价,采用在阴极射线管显示器上获得的颜色刺激,在5个不同明度的中性色背景下,标准刺激的明度L*从5到95以5个CIELAB单位为变化步长,
研究无压烧结条件下原位合成工艺对ZrB2/B4C陶瓷复合材料的烧结致密化、力学性能、显微组织的影响.结果表明材料的密度随着烧结温度的增加和保温时间的延长先增加后降低,在烧
为了寻求耐磨性能好的工程材料,应用自行设计的罐式固液冲蚀磨损装置研究了金属材料(结构钢40#)和工程陶瓷(S i3N4)的磨损及冲击波纹的发展过程。研究表明磨粒粒径大小和磨损