Variation of stress in attached copper film with an applied strain is measured by X-ray diffraction combined with a four-point bending method.A lower slope of the initial elastic segment of the curve of X-ray measured stress versus applied strain results from incomplete elastic strain transferred from the substrate to the film due to insufficiently strong interface cohesion.So the slope of the initial elastic segment of the X-ray stress (or X-ray strain directly) of the film against the substrate applied strain may be used to measure the film-substrate cohesive strength.The yield strength of the attached copper film is much higher than that of the bulk material and varies linearly with the inverse of the film thickness.
Variation of stress in attached copper film with an applied strain is measured by X-ray diffraction combined with a four-point bending method. A lower slope of the initial elastic segment of the curve of X-ray measured stress versus applied strain results from incomplete elastic strain transferred from the substrate to the film due to insufficiently strong interface cohesion. so the slope of the initial elastic segment of the X-ray stress (or X-ray strain directly) of the film against the substrate applied strain may be used to measure the film-substrate cohesive strength. The yield strength of the attached copper film is much higher than that of the bulk material and varies linearly with the inverse of the film thickness.