Influence of Water Pollution on MIC of Stainless Steel 304L

来源 :Journal of Iron and Steel Research(International) | 被引量 : 0次 | 上传用户:zxf3896641
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The influence of water pollution and welding defects on MIC(rnicrobiologically influenced corrosion)was studied.The open circuit potential(OCP)was measured during MIC test.It was found that OCP shifted to a higher level when the system was inoculated with bacteria while the OCP of those samples in water without bacteria was kept at a low level.The OCP decreased dramatically when MIC started in polluted water.Combination of weld defect-heat tint,polluted water and adding bacteria causes MIC happen at high rate.Some elements inside the tubercle were analyzed with EDXA.The pits and biofilm were observed with SEM.Microbiological analysis revealed the difference of bacteria between corroded and uncorroded samples. The influence of water pollution and welding defects on MIC (rnicrobiologically influenced corrosion) was studied. Open circuit potential (OCP) was measured during MIC test. It was found that OCP shifted to a higher level when the system was inoculated with bacteria while the OCP of those samples in water without bacteria was kept at a low level. The OCP decreased dramatically when MIC started in polluted water. Combining of weld defect-heat tint, polluted water and adding bacteria causes MIC happen at high rate. Home elements inside the tubercle were analyzed with EDXA.The pits and biofilm were observed with SEM. Microbiological analysis revealed the difference of bacteria between corroded and uncorroded samples.
其他文献
混凝土砌块的生产在我国兴起的时间不长 ,因而其生产设备特别是大型的生产线 ,大都从国外引进 ,它在一定程度上促进了我国砌块产业的发展。从 90年代开始 ,国内也有一些工厂
三峡大学副校长谭志松教授的一书,以民族教育为视角,为中国劳动力转移研究带来了显豁的视野.
研究了冷轧变形对Ti强化马氏体时效不锈钢Custom 465时效析出、逆转变奥氏体相变和力学性能的影响。结果表明:①在510℃时效过程中,杆状Ni3Ti金属间化合物持续析出、长大,致
本文结合对三个国家行业标准的学习,介绍了不同种类的非承重内隔墙轻质条板的定义、类型、尺寸、原材料以及对条板的物理力学性能要求.
俗话说:干净瓦匠,邋遢木匠.早年有私人营造厂时,就常听如此说法.1959年北京建设十大工程,迎接中华人民共和国成立10周年,笔者在人民大会堂施工现场也曾听到如此说法.记得当时
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
由江苏省科委资助,苏州医学微生物学教研室张澜生教授负责的课题:“分泌抗人白血病细胞分化抗原单克隆抗体的杂交瘤试建”,于1989年12月12日在苏州市通过鉴定。以白血病细胞
低合金钢在不同的江面铁路桥上曝露 8年的结果表明 :导致江面铁路桥上腐蚀异常严重的主要环境因素是运行机车排放的SO2 。钢材的腐蚀率随环境中SO2沉积率的增加而增加 ,其中
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
患者,男性,48岁。因阵发性心前区闷压样疼痛半月余而就诊。疼痛每次发作时持续5~10分钟,不放散,口服硝酸甘油可缓解症状。既往无类似病史。体检:唇无紫绀,肺部正常,心界无扩