Iron ions were used as probes to explore the structural and magnetic properties of 70TeO2’25B2O3’ 5SrF2 vitreous matrix. The distribution of Fe3+ ions on different structural aggregates was revealed by means of EPR, as depending on Fe2O3 concentration. Strongly distorted octahedral sites were detected for the isolated paramagnetic ions, and also clusters of Fe ions especially at high Fe2O3 content of samples. Magnetic susceptibility measurements evidenced both dipoledipole and superexchange type interactions involving iron ions. Mixed valence states of iron ions were also detected
Iron ions were used as probes to explore the structural and magnetic properties of 70TeO2’25B2O3 ’5SrF2 vitreous matrix. The distribution of Fe3 + ions on different structural aggregates was revealed by means of EPR, as depending on Fe2O3 concentration. Strongly distorted octahedral sites were detected for the isolated paramagnetic ions, and also clusters of Fe ions especially at high Fe2O3 content of samples. Magnetic susceptibility measurements evidenced both dipoledipole and superexchange type interactions involving iron ions. Mixed valence states of iron ions were also detected