This article investigated effects of degrees of deformation, heat treatment temperatures and holding times on the recrystallization behavior of directionally solidified DZ4 superalloy. The results showed that, recrystallization of DZ4 superalloy could take place during solution heat treatment after certain degrees of cold work and depths of recrystallization increased with increasing degrees of deformation and heat treatment temperature. At the temperature below y’ solvus, prolonged holding times did not play an important role in improving recrystallization depths. Moreover, prevention measures for recrystallization of directionally solidified blades were given.
This article showed effects of degrees of deformation, heat treatment temperatures and holding times on the recrystallization behavior of directionally solid DZ4 superalloy. The results showed that, recrystallization of DZ4 superalloy could take place during solution heat treatment after certain degrees of cold work and depths of recrystallization increased with increasing degrees of deformation and heat treatment temperature. At the temperature below y ’solvus, prolonged holding times did not play an important role in improving recrystallization depths. Moreover, prevention measures for recrystallization of directionally solidified blades were given.