【摘 要】
：
The magnesium alloy has a unique advantage in 3C fields due to its high specific strength and excellent electromagnetic shielding characteristic.However,it is d
【机 构】
：
College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China;Z
论文部分内容阅读
The magnesium alloy has a unique advantage in 3C fields due to its high specific strength and excellent electromagnetic shielding characteristic.However,it is difficult to deform homogeneously because of hexagonal close-packed structure.In the present work,the microstructure,mechanical properties and stretch forma-bility of magnesium alloy sheets with different alloying elements were investigated.It was indicated that a trace addition of Zn or/and Er made a key role in modifying texture,activating shear bands formation and precipitating nanoscale second phases,respectively,which resulted in an obvious improvement in both stretch formability and mechanical properties.The results suggested that the Mg-0.5Zn-0.5Er alloy sheet exhibited higher tensile strength along the rolling direction,i.e.,yield strength of 180 MPa and ultimate tensile strength of 201 MPa,accompanying with superior Erichsen value of 7.0 mm at room tempera-ture.The good performances of the sheet were ascribed to weakening basal texture intensity,formation of shear bands and precipitation of nanoscale W-phase (Mg3Zn3Er2).
其他文献
文中提出了一种基于泡克耳斯效应的集成光学电压传感器测量直流电压的研究方案,光纤光路结构采用熊猫型保偏光纤与低偏光纤相结合以提高系统光路的互易性,理论上利用琼斯矩阵推导了入射光光路数学传输模型,得出干涉光强与干涉信号的关系表达式。针对该光学电压传感器设计方案,搭建了实验平台并对系统进行了0～15 V直流实验,实验结果表明该传感器输入电压与数字输出曲线之间具有良好的线性关系,最大非线性误差为0.2%,
Weight reduction plays an important role in reducing fuel and emissions,and the heat-treatable 6016 aluminum alloy exhibits excellent application prospect in automobile lightweight.In this paper,ingot with constant Mg/Si ratio and decreased Mg and Si cont
The metal-organic-decomposed lanthanum cerium oxide(LaCeO2)solution was spin-coated on p-type Si substrate to form thin films.The method of microwave-assisted annealing was adopted to modify the surface properties of the deposited thin films.Th
为了有效监测局部放电信号,利用FPGA的高速并行处理能力,设计一种基于FPGA的特高频局部放电监测硬件实现系统。文中介绍了系统的硬件设计及FPGA实现原理。系统使用提升小波变换对采集数据进行脉冲提取,然后对有效脉冲进行特征提取,最后将提取的特征参数送入PC端,使用DBSCAN将脉冲的特征提取结果进行聚类分离。实验结果表明,基于高速FPGA设计的局部放电监测硬件系统能将不同脉冲信号有效分离。
A novel phenomenon of spontaneous positive exchange bias(PEB)is reported in SrFeO3-x/SrCoO3-x epitaxial bilayer without undergoing any magnetic field treatment.When inserting a thick SrTiO3(STO)nonmagnetic spacer(about 6 nm)into the bilayer interface,this
The increase in zinc content in Al-Zn-Mg-Cu alloys provides an effective method to enhance the strength.Transmission electron microscopy(TEM)and tensile test were employed to analyze the microstructure and tensile properties,respectively,of Al-9.3 Zn-2.0
Rapid oxidation takes place both in the laboratory and in industrial conditions when alloy 925 is contaminated by oxide powder,and the oxidation rate is much higher than normal.Herein,the rapid oxidation behavior and mechanism of alloy 925 were investigat
The Ti51.44Zr16.26Cu30Sn2.3(at%)amorphous filler alloy in a ribbon form was prepared by melt spinning.The Ti-6 Al-4 V alloy was brazed in vacuum furnace by using the Ti51.44Zr16.26Cu30
Al2O3-ZrO2-TiO2 coatings were successfully prepared by plasma spraying Al2O3-ZrO2 composite powders with and without TiO2 addition.The effects of TiO2 on the ph
For the purpose of elevated temperature service and weight reduction in aerospace vehicle applications,a novel Ti-Zr-Fe-Cu-Ni-Co-Mo filler metal was employed to join TiAl to Ni-based superalloy(GH536).The effects of brazing temperature on interfacial micr