The effect of vanadium content on the microstructure and hydrogen absorption/desorption properties in Ti-V-Cr alloys was studied. The results show that with the
【机 构】
：
State Key Laboratory for Advanced Metals and Materials
论文部分内容阅读
The effect of vanadium content on the microstructure and hydrogen absorption/desorption properties in Ti-V-Cr alloys was studied. The results show that with the increase of vanadium content from 5at.%, 10at.% to 35at.%, the hydrogen absorption capacity increases gradually from 1.14wt.%, 1.57wt.% tO2.84wt.%, and the hydrogen desorption capacity also increase from 0.43, 0.64, to 1.59. This indicates that the alloy with 35at.% vanadium content has the most optimum hydrogen storage capacity among these alloys. The microstructure observation also indicates that the alloy with 35at.% vanadium turns to be the single-phase alloy of the BCC solid solution. Furthermore, with the increase of vanadium content the pressure plateau becomes more distinguishing and shifts to lower pressure level gradually. The kinetics of hydrogen absorption was also found to be dependent with the vanadium content in these discussed alloys.
其他文献
The two series of as-deposited and annealed Ti/Co/Ti thin films were deposited by magnetron sputtering onto glass substrates at room temperature. The structural
series of (Ni50Fe50)x(SiO2)(1-x) films with different volume fraction x was fabricated by magnetron co-sputtering technique. The microstructure, magnetic and el
Nanostructured materials, characterized by an ultrafine grain size, have stimulated much research interest by virtue of their unusual mechanical, electrical, op
Silicon is the material most commonly used in the manufacturing of photovoltaic (PV) cells. In the current study, laboratory experiments of purification of sola
The Hi-B silicon steels were cold rolled by cross shear rolling (CSR) with different mismatch speed ratio(MSR)s and conventional rolling(CR) respectively, follo
Sintered permanent magnetic strontium ferrites were studied using transmission electron microscopy to investigate the microstructure morphology and its correlat
The effect of sintering process (especially the sintering temperature) on the magnetic property and microstructure of sintered sample of nanosized soft magnetic
Support vector machine has become an increasingly popular tool for machine learning tasks involving classification, regression or novelty detection. Training a
Fe3O4 nanoparticles were prepared by chemistry co-precipitation and the mean crystal size was 17.9 nm measured by XRD. After it had been treated by silane-coupl
The effect of heat treatment on microstructure, equilibrium hydrogen sorption pressure and plateau slope of LaNi3.8Al0.75Mn0.45 alloy was investigated. X-ray di