【摘 要】
：
本文用光致发光谱（ＰＬ）结合俄欧电子能谱（ＡＥＳ）和Ｘ射线光电子能谱（ＸＰＳ），首次研究了Ｓ２Ｃｌ２钝化的ＧａＡｓ（１００）表面．结果表明，ＰＬ强度较钝化前样品提高了将近两个数量级．钝化后的表面ＡＥＳ谱显示含有Ｓ，Ｇａ，ＡＳ，Ｃ和少量Ｃｌ原子而不含Ｏ原子．ＸＰＳ谱说明
【机 构】
：
复旦大学应用表面物理国家重点实验室，复旦大学李政道物理综合实验室，东北林业大学物理系
论文部分内容阅读
本文用光致发光谱（ＰＬ）结合俄欧电子能谱（ＡＥＳ）和Ｘ射线光电子能谱（ＸＰＳ），首次研究了Ｓ２Ｃｌ２钝化的ＧａＡｓ（１００）表面．结果表明，ＰＬ强度较钝化前样品提高了将近两个数量级．钝化后的表面ＡＥＳ谱显示含有Ｓ，Ｇａ，ＡＳ，Ｃ和少量Ｃｌ原子而不含Ｏ原子．ＸＰＳ谱说明Ｓ原子和Ｇａ、Ａｓ原子都成键．与（ＮＨ４）２Ｓ处理的比较结果显示，几秒钟的．Ｓ２Ｃｌ２处理即可达到或超过几十分钟（ＮＨ４）２Ｓ处理的钝化效果．
In this paper, the passivation of GaAs (100) surface by S2Cl2 was first studied by photoluminescence (PL) combined with AES and XPS. The results show that the PL intensity is about two orders of magnitude higher than that before passivation. The passivated surface AES spectrum shows that it contains S, Ga, AS, C and few Cl atoms but no O atoms. XPS spectrum shows that the S atom and Ga, As atoms are bonded. The comparison with (NH4) 2S treatment shows that for a few seconds. S2Cl2 treatment can reach or exceed dozens of minutes (NH4) 2S passivation effect.
其他文献
近年来,随着我省农村经济的好转,对花椒的需求量也迅速增加,市场上出现商品花椒供不应求的紧张状况。因此积极发展花椒生产,是多种经营,繁荣山区商品经济,尽快使山区群众富
牙克石林区的城镇建设,三十多年来有很大发展。截止到1984年末,除林城牙克石市外,还在大兴安岭西坡、东坡的丛山峻岭之中先后建成林区城镇居民点一百二十六处,其中局(镇)级
本文通过对氦氖激光器多纵模单纵模运转时腔内参数和上下能级粒子数的测量，研究这两种不同动转状态下的激光输出特性及上下能级粒子数差的变化规律，讨论如何获得高功率单纵模输
制作胆机时,有人会忽略一个重要问题,即电子管的高压延时间题。为了降低电源变压器的功耗,胆机常采用半导体二极管作为高压整流元件。在电子管预热期间。其阴极由于冷发射而
一、基本情况:1、陇川县1988年人工造林面积,经88年11月份和12月初林业部门检查验收后,当时落实上报的总面积为18400亩。在造林总面积中,国营造林面积4300亩(包括国营林场造
网络技术的迅猛发展促成了网络反腐的勃兴,这种新型反腐模式已成为我国反腐倡廉机制中不可或缺的部分。网络反腐是一把双刃剑,在取得成效的同时也面临了许多隐患,如何用好网
光子扫描隧道显微镜（ＰＳＴＭ）的研制及样品的显微成像研究郭宁，吴世法，夏德宽，初世超，徐绍华（大连理工大学，大连１１６０２３）高崧，姚骏恩，商广义，贺节，李成基（中国科学院科仪中心电镜室，北京１０００８０）光子扫描遂道显微镜
日本的三期会、新人会、青年座、伙伴等五个话剧团,从八月起在大阪、京都、神户、名古屋、东京等大城市演出了《戏剧春秋》,演员大都是有舞台经验的青年演员。日本各报刊作
介绍飞来峡水利枢纽部分建筑物地基的淤泥质软土的形成、分布及其工程特性所带来的工程问题与处理。
The formation and distribution of silt soft soil on the foundation
用ＩＣＢ外延技术在ＮａＣｌ（１００）和Ｓｉ（１１１）衬底上生长了ＣｄＴｅ单晶薄膜．Ｘ光衍射、电子背散射通道及ＲＨＥＥＤ都表明获得了良好的单晶结构及平滑膜面．外延取向关系为ＣｄＴｅ（１００）／ＮａＣｌ（１００）和ＣｄＴｅ（１１１）／Ｓｉ（１１１）．实验发现，生长温度小于２３０℃时，外延膜呈闪锌矿（立方）和钎锌矿