A new kind of hollow hydrogel microfiber with discontinuous hollow structure was prepared by an ice-segregation-induced self-assembly process. Monodisperse thermo-responsive hollow poly(N-isopropylacrylamide)(PNIPAM) microgels were first synthesized by seed precipitation polymerization using colloidal Si O2 nanoparticles as seeds, followed by removing the silica cores of the formed Si O2/PNIPAM core/shell composite microgels with hydrofluoric acid. Then, the discontinuously hollow hydrogel microfibers were produced by unidirectional freezing of 1 wt% hollow PNIPAM microgel aqueous dispersion in liquid nitrogen bath, followed by freeze-drying to remove the formed ice crystals. Many orderly arrayed dents were observed on the surfaces of the hydrogel microfibers by field-emission scanning electron microscopy, indicating that they are constructed by closely packed monodisperse hollow PNIPAM microgels. The effect of freezing method and the hollow microgel concentration in the aqueous dispersion on the morphological structure of the hollow hydrogel microfibers was investigated.
A new type of hollow hydrogel microfiber with discontinuous hollow structure was prepared by an ice-segregation-induced self-assembly process. Monodisperse thermo-responsive hollow poly (N-isopropylacrylamide) (PNIPAM) microgels were first synthesized by seed precipitation polymerization using colloidal Si O2 nanoparticles as seeds, followed by removing the silica cores of the formed Si O2 / PNIPAM core / shell composite microgels with hydrofluoric acid. Then, the discontinuously hollow hydrogel microfibers were produced by unidirectional freezing of 1 wt% hollow PNIPAM microgel aqueous dispersion in liquid Many orderly arrayed dents were observed on the surfaces of the hydrogel microfibers by field-emission scanning electron microscopy, indicating that they were constructed by closely packed monodisperse hollow PNIPAM microgels. The effect of freezing method and the hollow microgel concentration in the aqueous disper sion on the morphological structure of the hollow hydrogel microfibers was investigated.