【摘 要】
：
采用真空热蒸镀方法,制备了四种Delta掺杂结构OLED器件,其结构为:ITO/m-MTDATA(50nm)/LiF(xnm)/NPB(10nm)/Alq(5nm)/C545T(0.05nm)/Alq(55nm)/LiF(1nm)/Al,都获得了性能稳定
论文部分内容阅读
采用真空热蒸镀方法,制备了四种Delta掺杂结构OLED器件,其结构为:ITO/m-MTDATA(50nm)/LiF(xnm)/NPB(10nm)/Alq(5nm)/C545T(0.05nm)/Alq(55nm)/LiF(1nm)/Al,都获得了性能稳定的绿色OLED器件。从实验结果分析可知:绿色OLED器件的电流-电压(I-V)特性曲线、亮度-电压(L-V)曲线、亮度-电流(L-I)曲线及效率等光电性能随着LiF厚度的变化而随之改变。从其中总结规律,对OLED器件制作工艺有一定的指导作用。
Four types of Delta-doped OLEDs were fabricated by vacuum thermal evaporation. The structures were as follows: ITO / m-MTDATA (50nm) / LiF (xnm) / NPB (10nm) / Alq (5nm) / C545T ) / Alq (55nm) / LiF (1nm) / Al, a stable green OLED device was obtained. From the experimental results, it can be seen that the current-voltage (I-V) curve, L-V curve, L-I curve and efficiency of green OLED devices change with the thickness of LiF. From the summary of the law, the OLED device manufacturing process has a guiding role.
其他文献
综合考虑陆源碎屑物供给、内源碳酸盐岩没积、沉积物侵蚀与再沉积、重力流沉积以及构造升降和水平位移等诸多地质因素，建立了一个能够模拟各型盆地的综合数学物理方程式。采用
α-Fe_2O_3 nanocrystal was encapsulated by a block-copolymer, hydroxylated poly (styrene-b- butadiene-styrene) (HO-SBS) to fabricate composite microspheres with
运用自旋回波序列，得到一系列用盐水饱和的多孔岩芯的磁共振自旋密度象，可以直观、准确地观察岩芯的结构，并对象的信号强度与渗透率和孔隙度之间的相关关系进行了分析，发现它们之
30年来,我国水电建设虽然经过艰难曲折的道路,但总的来看,发展还是快的,至1981年底,全国水电装机容量达1,825万千瓦(500千瓦以上),发电量613亿度,占全国总发电量的20%,相当
一、需水分析和节水政策为了说明传统的经济分析,我们可以用图1A中的S_n供水曲线来说明平水时期的特性。假若我们取需水曲线的斜率为负,那么水价OA将能使所有按此水价所获得
以色列的水资源利用率达95％,为了增加可用水量,他研究了一些新型的水资源系统。 1948年以色列国刚建立时,以色列水管理和水研究当局“塔哈尔”(Tahal)的水管理专家们面临的第
一、概述二江泄水闸位于二江中右部及原葛洲坝岛的位置。泄水闸上游引渠及下游尾渠均系人工开挖的导流明渠。整个泄水闸的基础以及导渠渠底为粘土质粉砂质、砂岩与粘土岩互
概述葛洲坝坝址基岩属下白垩纪,地层系砾岩、砂岩、粉砂岩和薄层粘土岩互层。经勘探查明,在第一期工程的基岩中约有60层软弱夹层,按其岩性组合,泥化程度等不同特性,分为五种
前言自古以来,人类就利用岩洞。古时候地下建筑主要用于人类的居住,因为整体岩石为防卸野兽提供条件,并使洞室保持冬暖夏凉。今天,进行地下建筑,人们具有远为优良的机具。实
一、绿水河水电站高压钢管道的外压失稳绿水河水电站的高压钢管道由三段高压平洞和两段斜井组成(见图1),全长约1,300米,最大设计水头为381米(包括15%的动水头),管径为2.8、2