The primary objective of this paper was to study the mechanical properties and durability of the cement stabilized gravel by different compact method. The influence of rubber particle content on mechanical properties of samples was studied by compaction tests and freezing thawing recycle tests. Pore structure and fractal characteristic of mixture were analyzed quantitatively using mercury intrusion porosimetry(MIP). X-ray diffraction(XRD) was adopted to identify the composition phases. The morphology analysis in micro scale and elemental analysis of samples were carried out by scanning electron microscope(SEM). The optimum compressive strengths of rubber cement stabilized gravel(RCSG) with static compaction method and with vibratory compaction method were obtained by controlling compaction degree and vibration time, respectively. From the compaction tests, the vibratory compaction method is preferred compared with the static compaction method as better compressive strength can be improved by about 340%-360%. Besides, test results also reveal that compressive strength of samples with vibratory compaction method or static compaction method will decrease with the rubber particle bulk content increasing. The freezing thawing recycle tests indicate that freezing thawing resistance has been improved(frozen stability coefficient K has been increased from 0.89 to 0.97) by the addition of rubber particles. MIP tests show that the mean pore diameter and porosity of mixture have been increased from 70 to 250 nm and 9% to 24% respectively, with the rubber particles content increasing. Component analysis shows that the calcium silicate hydrate(CSH) is the predominant hydrate product with or without the addition of rubber particles. The primary objective of this paper was to study the mechanical properties and durability of the cement stabilized gravel by different compact method. The influence of rubber particle content on mechanical properties of samples was studied by compaction tests and freezing thawing recycle tests. Pore structure and fractal characteristic of mixture were analyzed quantitatively using mercury intrusion porosimetry (MIP). The morphology analysis in micro scale and elemental analysis of samples were carried out by scanning electron microscope (SEM) . The optimum compressive strengths of rubber cement stabilized gravel (RCSG) with static compaction method and with vibratory compaction method were obtained by controlling compaction degree and vibration time, respectively. From the compaction tests, the vibratory compaction method is preferred compared with the static compaction method as better compressive strength can be impro ved by about 340% -360%. Besides, test results also reveal that compressive strength of samples with vibratory compaction method or static compaction method will decrease with the rubber particle bulk content increasing. The freezing thawing recycle tests indicate that thawing thawing resistance has been improved (frozen stability coefficient K has been increased from 0.89 to 0.97) by the addition of rubber particles. MIP tests show that the mean pore diameter and porosity of mixture have been increased from 70 to 250 nm and 9% to 24% respectively, with the rubber particles content increasing. Component analysis shows that the calcium silicate hydrate (CSH) is the predominant hydrate product with or without the addition of rubber particles.