研究了O′ Sialon ZrO2 SiC复合材料在不锈钢液中的侵蚀行为。造成侵蚀的原因主要是不锈钢液通过侵蚀通道向材料内部扩散。分形研究表明 ,材料侵蚀界面的分形维数在 1 2 5～ 1 30之间且与侵蚀过程存在相应关系。
The corrosion behavior of O ’Sialon ZrO2 SiC composites in stainless steel was investigated. The main reason for the erosion is that stainless steel liquid diffuses into the material through the erosion channel. Fractal studies have shown that the fractal dimension of the erosion interface is between 125 and 130 and is related to the erosion process.