The 3D needled C/SiC brake materials modified with graphite were prepared by a combined process of the chemical vapor infiltration, slurry infiltration and liqu
【机 构】
：
National Key Laboratory of Thermostructure Composite Materials,Xi'an Aviation Brake Technology Co.
论文部分内容阅读
The 3D needled C/SiC brake materials modified with graphite were prepared by a combined process of the chemical vapor infiltration, slurry infiltration and liquid silicon infiltration process. The microstructure and frictional properties of the brake materials were investigated. The density and open porosity of the materials as-received were about (2.1±0.1) g/cm3 and (5±1)%, respectively. The brake materials were composed of 59% C, 39% SiC, and 2% Si (mass fraction). The content of Si in the C/SiC brake materials modified with graphite was far less than that in the C/SiC brake materials without being modified with graphite, and the Si was dispersed. The braking curve of the 3D needled C/SiC modified with graphite was smooth, which can ensure the smooth and comfortable braking. The frictional properties under wet condition of the 3D needled C/SiC modified with graphite showed no fading. And the linear wear rate of the C/SiC modified with graphite was lower than that of the C/SiC unmodified.
其他文献
The thermal debinding behavior of stainless steel foam precursor in vacuum was studied and compared with that in hydrogen. The formation cause of pore channel w
The rare earth ternary complex of Eu3+ with thenoyltrifluoroacetone, and 4, 7-2NH2 phenanthroline was synthesized and well characterized by UV, fluorescent, IR
An aluminium alloy and its composite with dispersed SiC particles made by liquid metallurgy route were extruded under optimized conditions.The properties were c
The grain growth morphology, kinetics and texture change after uniaxial compression at 430 ℃ of an extruded AZ31 alloy were studied. The samples were loaded fo
Nanostructured zirconia top coat was deposited by air plasma spray and NiCoCrAlTaY bond coat was deposited on Ni substrate by low pressure plasma spray. Nanostr
The initiation sites and influencing factors of cavity nucleation were investigated for a Ti-6Al-2Zr-1Mo-1V alloy with lamellar starting structure, using the is
A new metastable β type titanium alloy called TB-13 with the combination of excellent strength and ductility was developed successfully. In order to develop a
The hydrothermal synthesis of single-crystalline β-MnO2 nanorods and their chemical conversion into single-crystalline LiMn2O4 nanorods by a simple solid-state
An optimization method was presented for cold stretch forming of titanium-alloy aircraft skin to determine process parameters and to reduce springback. In the o
The influence of gravity on the reaction engineering of tubular reactor is studied by analyzing the residence time distribution curves. The results show that up