采用浸泡腐蚀、极化曲线和应力腐蚀等方法研究时效对纳米TiC/Ti细化Al-Zn-Mg-Cu合金耐蚀性的影响.结果表明,峰时效态和过时效态细化合金在3.5％的NaCl溶液中浸泡192 h,腐蚀速率分别为0.756 5 mm/a和0.361 3 mm/a.峰时效态化合金在NaCl和NaCl+ H2O2溶液中的应力断裂时间分别为72.2 h和50.1 h;过时效态为221.2 h和80.8h,过时效态合金抗应力腐蚀性能高于峰时效态的.峰时效添加TiC/Ti细化合金后晶界较宽的PFZ(无沉淀析出带)降低其耐蚀性,过时效态晶界不连续且粗大的η相以及较窄的PFZ使合金耐蚀性提高.“,”Effects of aging on corrosion behavior of a novel nano TiC/Ti refiner refined Al-Zn-Mg-Cu alloy were investigated by means of soaking corrosion,polarization curve and stress crack corrosion.The results indicate that after soaked in 3.5％ NaCl solution for 192 h,the corrosion rate of peak-aged and over-aged Al-Zn-Mg-Cu alloy refined with TiC/Ti reach 0.756 5 mm/a and 0.361 3 mm/a respectively.The fracture time of stress crack corrosion are 72.2 h and 50.1 h with the peak-aged alloy refined with TiC/Ti at NaCl and NaCl-+-H2O2 solution,respectively,while at over-aged,they are 221.2 h and 80.8 h,respectively.The resistance of stress crack corrosion at over-aged is the higher than that of ones at peak-aged.The wider PFZ can decrease significantly the corrosion resistance of alloy refined with TiC/ Ti at peak-aged,however,at over-aged,the coarse and discontinuous phase preciphated from grain boundary and the narrow PFZ can improve the corrosion resistance.