论文部分内容阅读
Microstructure and phase transformation behaviors of the film annealed at different temperatures were studied by X-ray diffractometry (XRD), transmission electron microscopy and differential scanning calorimeter (DSC). Also tensile tests were examined. For increasing annealed temperature, multiple phase transformations, transformations via a B19-phase or direct martensite/austenite transformtion are observed. The TiNiPd thin film annealed at 750℃ had relatively uniform martensite/austenite transformtion and shape memory effect. Martensite/austenite transformtion was also found in strain-temperature curves. Subsequent annealing at 450℃ had minor effect on transformation temperatures of Ti-Ni-Pd thin films but resulted in more uniform transformation and improved shape memory effect.