In this study,an efficient catalyst Ag@g-C3N4 nanocomposite was successfully synthesized through a simple green reaction,and the characterizations through XRD,FTIR,SEM,BET and XPS were also studied.The activities of Ag@g-C3N4 were investigated toward the
【机 构】
:
College of Chemistry,Chemical Engineering and Environment,Minnan Normal University,Zhangzhou 363000,
论文部分内容阅读
In this study,an efficient catalyst Ag@g-C3N4 nanocomposite was successfully synthesized through a simple green reaction,and the characterizations through XRD,FTIR,SEM,BET and XPS were also studied.The activities of Ag@g-C3N4 were investigated toward the reduction of 4-nitrophenol to their corresponding aminophenol compounds in the presence of excess NaBH4 as a reducing agent.The Ag@g-C3N4 nanocomposites exhibited high catalytic activities,in which a 92.2% 4-nitrophenol conversion in 10 min and the apparent rate constant Kapp =264.27×10-3 min-1 were obtained.The as-prepared Ag@g-C3N4 nanocomposites showed great potential in catalytically inducing the reduction of 4-nitrophenol,which makes them economically and energy conservation attractive from industrial waste water treatment.
其他文献
为了提高多模复合导引头跟踪模式复杂逻辑决策的适应性,采用随机森林构建模式决策网络、结合误差补偿的方法,对传统的人工条件判读流程进行了优化,提高了模型的分类准确率,并将该方法应用到复合导引头中进行理论分析和仿真验证.结果表明,得到的跟踪模式的分类正确率达100%,运行速度提升16%,代码量减少3倍;基于随机森林和误差补偿的跟踪模式决策方法对导引头跟踪模式决策具有较好的适应性,可以高效实现跟踪模式的自主决策.此研究算法为高效率地实现导引头跟踪模式决策提供了参考.
为了研究工艺参量对激光熔覆Ni60涂层裂纹及厚度影响,采用在45#钢基材表面熔覆Ni60合金粉末的正交试验方法,分析了影响裂纹产生的工艺参量的主次因素以及影响涂层厚度的主要因素,并对试验结果进行极差分析,获取了裂纹最少的最优工艺参量.结果表明,影响裂纹产生的主次因素为扫描速率>送粉速率>激光功率,裂纹最少的工艺参量为激光功率1400W,扫描速率4.0mm/s,送粉速率为1.0r/min,此时,在熔覆起始位置出现了一条短裂纹;对涂层厚度的影响程度主次因素为送粉速率>扫描速率>激光功率;经测量,熔覆层的硬度是
为了提高光纤光栅传感器的传感精度,降低温度对压变传感器交叉敏感性的影响,提出一种具有自温补性能的菱形结构压变传感器.采用有限元法、利用ANSYS软件对菱形结构分别进行静力及受热分析,结合自温补机理,研究菱形边长、厚度对灵敏度的影响,经仿真确定传感器的边长为7mm、厚度为1mm.结果表明,菱形结构具有温度自补偿性,最终设计的传感器微小形变量可低至7.9669×10-8 mm.相较于传统传感器,该传感器具有温补性能、抗干扰能力强等特性,可在检测局部应力、工程结构缺陷以及航天航空传感中具有重要应用.
A highly selective iron ions fluorescent probe based on the benz(c)acridine-1,2,3-triazole derivatives was produced by multi-step reactions.1-(7-Benz[c]acridinyl)-4-(4-methylphenyl)-1,2,3-triazole (4a),C26H18N4,was structurally determined by single-crysta
为了提高电站锅炉自动化程度,为真实锅炉的优化控制提供新颖的实时在线测量手段,采用计算机层析重建和激光吸收光谱技术相结合的方法,进行了理论分析和实验验证.仿真实验证明了仅采用2个投影方向即能够实现温度峰值位置的重建及其相对高低的分辨;布置6条测量路径形成测量网格,得到真实锅炉炉膛的实时在线2-D温度场重建数据.结果表明,炉膛平均温度与锅炉蒸汽流量的相关系数达到0.91,回归分析得到决定系数为0.88;可将平均温度作为炉膛内实时的总辐射能的表征,用于避免锅炉超调,根据温度可获知燃料总的热值波动,2-D温度场的
对2020年1-3月CLDAS多源降水融合实况、多源气温融合实况采用平均绝对误差分析、均方根误差分析及相关系数分析等方法进行检验评估,并与2019年同时段多源降水融合实况、多源气温融合实况进行对比分析.结果表明:2月降水多源融合实况较观测实况偏多;3月多源气温融合实况最接近观测实况;西部地区的日最低气温多源融合实况较为接近观测实况.
利用白山市各观测站1981—2019年的逐日平均气温、平均相对湿度、平均风速及平均日照时数计算白山市逐月温湿指数、风寒指数、穿衣指数,选取熵权法对12个月的3项指数进行权重分配,从而建立旅游气候舒适度评价模型并分析白山市旅游气候资源优势.结果表明:白山市5—9月为舒适期,10月为较舒适期,3月、4月、11月为较不舒适期,1月、2月、12月为不舒适期.6—8月白山市平均舒适天数为63 d,舒适和较舒适的天数占比达95.7%.
利用2016年1月1日—2018年12月31日吉林省381个站的逐日最高气温、最低气温和定时气温的观测数据,对ECMWF高分辨率模式的2 m最高、最低气温和定时气温预报进行检验分析.结果表明,ECMWF模式对吉林省的气温预报与实况存在一定偏差;从空间上看,自西向东气温预报准确率逐渐递减,预报误差逐渐增大;从时间上看,随预报时效的增长,预报准确率逐渐下降.对ECMWF的气温预报进行高度差订正后,模式最高气温24 h、48 h、72 h的预报准确率分别从52%、51%、50%提高至58%、56%、54%;最低
利用吉林省2003—2018年春季土壤湿度数据及同期的气温、降水数据,分析了春季土壤湿度的时空分布特征及其与气候因子的关系。结果表明:吉林省春季土壤湿度总体上呈西低东高分布趋势,16 a无明显趋势变化,2010年是土壤由适宜、轻旱向适宜、偏湿状态发展的转折期。春季土壤湿度与降水量呈正相关关系,与平均气温为负相关关系。季节尺度上,影响春季土壤湿度的主要气候因子是前一年秋季和冬季降水量、前一年冬季平均
It is very hard to obtain uniformly dispersed conductive polymer nanocomposites because of the accumulation tendency of nanomaterials.In current work,the aramid nanofiber/silver nanowire composite film was prepared by mixing evenly through the solution an