Hot compression tests were conducted on a Gleeble-1500 simulator to investigate the hot deformation behavior of BT20 Ti alloy (Ti-6Al-2Zr-1Mo-1V) in the tempera
【机 构】
:
School of Materials Science and Engineering
论文部分内容阅读
Hot compression tests were conducted on a Gleeble-1500 simulator to investigate the hot deformation behavior of BT20 Ti alloy (Ti-6Al-2Zr-1Mo-1V) in the temperature range from 550 to 1000℃ at constant strain rate in the range of 0.01~1 s-1, and then the optimum spinning temperature range was determined. Moreover, tube spinning experiments were executed to verify the reasonability of the optimum temperature range. The results show that the flow stress declines gradually with increasing deformation temperature and decreasing strain rate. In α+β phase region the dynamic recrystallization is the main softening mechanism and in β phase region the hot deformation softening is controlled by dynamic recovery. In α+βphase region with reducing strain rate dynamic recrystallization is fully developed. The optimum temperature of hot spinning is 850~900℃ and that of warm spinning is 600~650℃.Meanwhile, at the temperature above 600℃ tubular workpieces of BT20 Ti alloy have been spun without surface cracks and microstructure inhomogeneity, which proves that the optimum spinning temperature range obtained through hot compression experiments is reasonable.
其他文献
Ti-50.6Ni(molar fraction, %) shape memory alloy solution treated at 850℃ for 1h followed by ageing treatment at 450℃ for 3h was studied with differential scan
Nickel-metal hydride (Ni/MH) batteries are one of promising batteries for electric vehicle applications, but at high temperature the charge efficiency of nickel
2014 Al alloy of 8mm in thickness was successfully welded by friction stir welding method. The experimental results show that the tensile properties of the join
The properties of trimethyl phosphate(TMP)-based nonflammable electrolytes with LiPF6 as solute were investigated using graphite anode and LiCoO2 cathode. The e
Enantioselective hydrogenation of ethyl 2-oxo-4-phenylbutyrate to ethyl (R)-2-hydroxy-4-phenyl- bu-tyrate on Pt/γ-Al2O3 modified by 10,11-dihydrocinchonidine w
The first measurement of impedance on free-standing diamond films from 0.1 Hz to 10 MHz up to 300℃ were reported. A wide range of chemical vapour deposition (C
In this paper, Bezier basis with shape parameter is constructed by an integral approach. Based on this basis, we define the Bezier curves with shape parameter.
The effects of preparation and crystal growth methods on the microstructure, composition, and oxidation of CoTi(Zr)intermetallics were dealt with. A group of me
Given a set of triangles and a rectangle container, the triangle packing problem is to determine ifthese triangles can be placed into the container without over
A multi-component Cu-based metal powder was chosen for direct laser sintering. The powder consists of a mixture of high-purity Cu powder, pre-alloyed CuSn and C