【摘 要】
：
The microstructure and high-temperature tensile property of a Ti-47Al-2Cr-2Nb alloy fabricated via selec-tive electron beam melting (SEBM) with hatch spacings of 85,100,and 115 μm were systematically investigated.When the hatch spacing increased from 85 t
【机 构】
：
School of Materials Science and Engineering,Jiangsu University of Science and Technology,Zhenjiang 2
论文部分内容阅读
The microstructure and high-temperature tensile property of a Ti-47Al-2Cr-2Nb alloy fabricated via selec-tive electron beam melting (SEBM) with hatch spacings of 85,100,and 115 μm were systematically investigated.When the hatch spacing increased from 85 to 115 μm,the microstructure comprising the horizontal cross section changed from coarse lamellar (γ/B2) colonies to an inho-mogeneous structure and the grain morphology trans-formed from elongated grains to inhomogeneous and equiaxed grains along the building direction of the vertical cross section.The boundary population of the SEBM-produced TiAl alloy samples was dominated by high-angle grain boundaries (≥ 15°),and the volume fraction of these boundaries decreased with hatch spacing increasing.Additionally,the as-built TiAl alloy sample produced under a spacing of 100 μm exhibited the highest room-and elevated-temperature tensile strengths,with the ultimate tensile strength at room temperature (642 MPa) increasing to 674 MPa at 700 ℃.Furthermore,the mechanism of anomalous strengthening at 700 ℃ was discussed in detail.
其他文献
Surface Ag granular packs (SAgPs) have been fabricated from dual-phase Ag35.5Zn64.5 precursor alloy consisting of both ε and γ phases by using a facile one-step triangle wave potential cycling in 0.5 mol·L-1 KOH.During the continuous potential cyclic swee
Mn-doped ZnO samples,Zn1-xMnxO (x =0,0.01,0.03 and 0.05;mole fraction),were successfully synthesized by sonochemical method.The undoped and Mn-doped ZnO samples were characterized by X-ray diffraction (XRD),scanning electron microscopy (SEM),transmission
Coaxial FezO3/TiO2 nanotubes (Fe2O3/TiO2 NTs) were prepared by two anodic oxidation processes.The synthesized Fe2O3/TiO2 NTs catalysts showed high photocatalytic activity in heterogeneous photo-Fenton system.With the help of Fe2O3/TiO2 NTs,4-nitrophenol(1
Although Ni-Ti-O nanopores (NPs) can be fabricated by anodization of mechanically polished NiTi alloys,the top disordered layer is difficult to remove thus hindering the functionality of the Ni-Ti-O NPs.In this work,an electropolishing (EP) pretreatment w
The present work introduces a novel γ\'phase-strengthened Ir-W-Al-Th superalloy for ultrahigh-temper-ature applications.First,the as-cast microstructure and phase transformation of Ir-13W-6Al-0.15Th (at％) alloy during solid solution and aging were inves
It is confirmed that the solid solution tempera-ture range to obtain optimal magnetic properties is different for the magnets with different Fe contents,and the corre-lation between magnetic properties and microstructures influenced by solid solution temp
The aim of this study is to develop processing maps based on two models and compare them with con-ventional processing maps.The hyperbolic sinus constitu-tive equation and artificial neural network (ANN)approaches were used in this investigation to predic
High strength titanium alloys suffer from a limited combination of strength and ductility.Considering their microstructure,the coarse β grain is a detrimental factor.In the present study,the effects of hot deformation and annealing treatment on the β grai
The uniaxial tensile deformation behavior of a sandwich-like structural TiNb-NiTi composite was inves-tigated by uniaxial tensile test and in situ high-energy synchrotron X-ray diffraction (SXRD).It is found that below 1.2％ macroscopic strains,the elastic