Low cycle fatigue tests on nickel base superalloy GH536 were performed at 600, 700 and 800℃. The strain-life and cyclic stress-strain relationship were given at various temperatures. The change in fatigue life behavior and fatigue parameters with tem- perature increasing was discussed. At low and intermediate total strain amplitudes, the fatigue life was found to decrease with increasing temperature.
Low cycle fatigue tests on nickel base superalloy GH536 were performed at 600, 700 and 800 ° C. The change in fatigue life behavior and fatigue parameters with tem- perature increasing was discussed. At low and intermediate total strain amplitudes, the fatigue life was found to decrease with increasing temperature.