【摘 要】
：
在稀土镁合金专用熔剂覆盖和氩气保护下制备了Mg-7Gd-3Y、Mg-7Gd-3Y-0.5Zr两种合金。采用光学显微镜、X射线衍射、室温力学测试对合金的显微组织与力学性能进行了分析,研究了
论文部分内容阅读
在稀土镁合金专用熔剂覆盖和氩气保护下制备了Mg-7Gd-3Y、Mg-7Gd-3Y-0.5Zr两种合金。采用光学显微镜、X射线衍射、室温力学测试对合金的显微组织与力学性能进行了分析,研究了Zr元素对合金晶粒大小及铸态力学性能的影响。结果表明,Zr可以极大地细化Mg-7Gd-3Y合金的晶粒;Zr元素的添加,使合金铸态下的抗拉强度和伸长率均得到了较大提高。
Mg-7Gd-3Y and Mg-7Gd-3Y-0.5Zr alloys were prepared under the flux covering of rare earth magnesium alloy and argon gas protection. The microstructure and mechanical properties of the alloy were analyzed by optical microscope, X-ray diffraction and room temperature mechanical tests. The effects of Zr on the grain size and the as-cast mechanical properties of the alloy were studied. The results show that Zr can greatly refine the grains of Mg-7Gd-3Y alloy. The addition of Zr increases the tensile strength and elongation of the alloy as-cast.
其他文献
异位妊娠是妇产科常见的急腹症,是孕产妇死亡的主要原因之一.重复异位妊娠是指首次异位妊娠患者经手术或保守治疗后,再次在宫体外的输卵管、卵巢或腹腔内妊娠.
通过扫描电镜对失效的lycoming发动机配重挡片进行断口形貌和金相组织分析。结果表明,该发动机配重挡片失效是疲劳断裂。结合其使用特点分析认为:挡片材料热处理不当、结构设
采用光学显微镜、扫描电镜、能谱仪并结合宏观断口观察,对50Z钢制造的汽车锥齿轮断齿的原因进行了分析。分析表明,由于淬火热处理不规范,引起齿轮齿尖产生细小裂纹,在外力作
目的研究胎儿心动过速的临床治疗方案。方法回顾性分析2011年1月至2015年12月在广州医科大学附属第三医院胎儿医学科进行系统超声检查的45 566例孕妇的结果，59例(3.62‰)通过胎儿超声心动图和M型超声诊断为胎儿心律不齐，其中12例诊断为胎儿室上性心动过速(superventricular tachycardia, SVT)，对3例SVT病例分别给予盐酸普罗帕酮、美托洛尔和地高辛治疗，另外
对开裂失效模具的断口形貌及显微组织进行了分析。结果表明:模具材料存在缩口、疏松等冶金缺陷,电火花加工后的变质层,在成形过程中齿形型腔受径向拉应力且分布集中是凹模发
针对102钢高温过热器内壁氧化皮脱落造成堵管而引起的爆管事故,采用扫描电镜(SEM)、金相显微镜、能谱仪(EDS)对氧化皮的结构和成分进行分析,从材料和实际运行的角度,对内壁氧
通过高温拉伸试验研究TC4钛合金激光对接接头超塑性变形,用金相显微镜观察了超塑性变形前后母材及焊缝显微组织,并测量了变形前后焊缝截面的显微硬度。结果表明:激光焊接接头
研究了CuNiMnSi合金的相结构、加工特性及钎焊性能。结果表明,该合金在晶界及晶内都有第二相析出,第二相主要为Ni3Si相,还有少量Ni31Sil2相,合金加工存在600～700℃中温脆性区
采用金相显微镜、透射电镜和硬度等测试手段,研究了Al-Zn-Mg合金在120 MPa液态模锻成形,经T6处理后的合金组织与性能。结果表明:试样热处理后,在晶内析出了细小球形GP区及η
对挤压ZAl6合金在不同加工量下冷拔加工后的组织和力学性能进行了研究.结果表明:ZAl6合金铸态组织为基体η相和网状分布的白色α相,无网状共晶组织(β+η)相出现;材料的抗拉