【摘 要】
:
Based on the experimental analysis and theoretical calculation,the self-propagating high temperature synthesis of TiB2/Fe composite was studied.The experimental results show that the interfacial between TiB2 and Fe was smooth and clear,and the composite b
【机 构】
:
State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049,
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
Based on the experimental analysis and theoretical calculation,the self-propagating high temperature synthesis of TiB2/Fe composite was studied.The experimental results show that the interfacial between TiB2 and Fe was smooth and clear,and the composite bending strength increased with the addition of Fe,however,the hardness decreased accordingly.The thermodynamics of the composites preparation process was calculated.The calculation results show that the primary chemical reaction was the reaction between Ti and B.The extra B can react with Fe,producing the brittle phase Fe2B.By increasing Ti,the production of Fe2B will decrease and a few of Ti-Fe intermetallic compound will be produced by the reaction between Ti and Fe in the composites.Finally,according to the Merzhanov condition of the adiabatic system,it is concluded that the Fe content must be selected between 16.3% and 54.3% by the thermodynamics temperature of reaction calculation.
其他文献
The present work presents the microstructure of β-Ca2SiO4 (β-C2S) after accelerated carbonation.The synthesis procedure of β-C2S was examined first,and the crystalline and amorphous structure,the distribution and the pore structure ofβ-C2S carbonation pro
The SnO2 quantum dots (SnO2QDs)/ZnS nanosheets (ZnSNs) heterojunction was fabricated via an in-situ synthetic method at room temperature. Rhodamine B, potassium dichromate, and tetracycline were used to discuss the photocatalytic activities of the as-prep
Nitrogen and sulfur co-doped porous nanocarbon (ZIF-C-N-S) catalyst was successfully synthesized derived from ZIF-8 and thiourea precursors. The electrochemical measurements indicate that the as-obtained ZIF-C-N-S catalyst exhibits higher electrocatalytic
A novel aqueous Sn-S complex solution was applied as precursor to fabricate SnO2 electron selective layers (ESLs) for the hybrid perovskite solar cells (PSCs). The tin and sulfur powder were directly dissolved in a (NH4)2S water solution to form Sn-S prec
Three different kinds of sepiolite (Type A, Type B and Sepiolite fiber) were processed by calcination and analyzed by thermogravimetric analysis (TG), X-ray diffraction diffractometer (XRD), scanning electron microscopy (SEM), BET (specific surface area f
Herein, two nanoparticles with different dimensions, spherical carbon dots (C-dots) and sheet-like hectorite clay, were used as physical crosslinkers to fabricate C-dots-clay-poly(N-isopropylacrylamide) nanocomposite hydrogels (coded as C-dots-clay-PNIPAm
To evaluate the property and degradation characteristics of concrete prepared with aggregate contained montmorillonite,concretes were prepared with aggregates contained montmorillonite,and then concrete slump loss,compressive strength,electric flux,the re
2198 and 5A90 Al-Li alloys were anodized with a constant DC potential in 18%H2SO4 solution (Solu.A) and the mixture solution of 18%H2SO4+5%C2H2O4 (Solu.B) at room temperature.12 and 11 V was optimized as the applied oxidation potential for 2198 and 5A90 a
A niobate/titanat nanoflakes (Nb/TiNFs) composite was synthesized via the hydrothermal method and used to remove Pb(II) from water. XRD, TEM, and SEM results indicate that Nb/TiNFs appear as nanoflakes, of which the primary crystal phase is tri-titanate.
The modification of graphitic carbon nitride can significantly improve the photocatalytic performance of graphitic carbon nitride (g-C3N4). Fe2O3/nitrogen-deficient g-C3N4-x composite catalysts were prepared with dicyandiamide as the precursor and Fe3+ do