【摘 要】
：
The semisolid A356 alloy strip was prepared by a novel continuous micro fused-casting process. The microstructure evolution and mechanical property of A356 aluminum alloy strip with different nozzle temperatures were investigated. The nozzle temperature h
【机 构】
：
Henan Key Laboratory of Research for Central Plains Ancient Ceramics, Pingdingshan University, Pingd
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The semisolid A356 alloy strip was prepared by a novel continuous micro fused-casting process. The microstructure evolution and mechanical property of A356 aluminum alloy strip with different nozzle temperatures were investigated. The nozzle temperature had great influences on the microstructure and property primarily accompanied with the crystal change in the fused-casting area through the cooling conditions. The results showed that the semisolid A356 alloy strip samples fabricated by micro fused-casting demonstrated good performances and uniform structures with the nozzle temperature at 593 ℃ and the stirring velocity at 700 r/min. The fine grains of the primary α-Al phase with average grain size of 51 μm and shape factor up to 0.71 were obtained under the micro fused-casting process, and the ultimate average vickers hardness came up to 83.39±0.89 HV, and the tensile strength and elongation of the A356 alloy strip reached 245.32 MPa and 7.85％, respectively.
其他文献
To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced polypropylene (GF/PP) composites, tensi
The use of the thermal power plant ashes including fly ash (FA) and bottom ash (BA) for producing unfired building bricks (UBB) using sodium hydroxide (NaOH) solution as an alkaline activator was investigated. A low applied forming pressure of 0.5 MPa and
The effect of homogenization treatment on the corrosion behavior and corrosion mechanism of Mg-Y alloys in 3.5 wt％ NaCl solution was investigated by electrochemical characterization, immersion testing and SEM observations. The diffusion kinetics model of
To decrease the modulus and increase the mechanical properties of recycled PET by introducing the flexible segments, the recycled polyethylene-terephthalate (PET) was modified by the chain extender produced with 2, 4, 6, 8-tetramethyl-2, 4, 6, 8-tetra (2,
The aging behavior of single lap joints (SLJ) in hygrothermal cycles was investigated and compared by using a shearing strength test, Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TG/DTG), energy dispersive spectrometry (EDS)
MoO2 nanocrystals (NCs) on Ni foam were simply synthesized via a facile hydrothermal method and a dip-coating method. It was worth noting that ultrafine interconnected MoO2 nanocrystals (about 10 nm) were uniformly anchored on Ni foam to fabricate a parti
The crystal structure, band structure, density of states, Mulliken charge, bond population and optical properties for LiBi1-xMxO3 (M=V, Nb, and Ta) were investigated using hybrid density functional theory. It was found that LiBiO3 doped with V, Nb, and Ta
A diamond-like carbon (DLC) film was deposited on YT14 substrate using magnetron sputtering (MS). The surface morphologies, roughness and bonding spectra of obtained film were characterized using scanning electron microscopy (SEM), atomic force microscopy
The effects of circulating fluid bed (CFB) ash on the adsorption performance of polycarboxylate superplas-ticiser and the mechanism of this influence on the dispersive property of the polycarboxylate superplasticiser were investigated by determing the cem