【摘 要】
:
The effects of 0.01–0.11 wt.%Zr on the inclusions, microstructure, tensile properties, and impact toughness of the China low activation martensitic steel were i
【机 构】
:
School of Metallurgical Engineering,Xi’an University of Architecture and Technology,Xi’an 710055,Sha
论文部分内容阅读
The effects of 0.01–0.11 wt.%Zr on the inclusions, microstructure, tensile properties, and impact toughness of the China low activation martensitic steel were investigated. Results showed that Zr exhibits good deoxidation and desulfurization abilities. The scanning electron microscope was used to examine the inclusions in the ingots. The main inclusions in the alloys were Zr–Ta–O, Zr–O, and Zr–O–S. However, some blocky Zr-rich inclusions appeared in Zr-2 and Zr-3 alloys. Typical martensitic structures were observed in the alloys, and average prior austenite grain sizes of 21.1, 15.7, and 14.8μm were obtained for Zr-1, Zr-2, and Zr-3 steels, respectively. However, increasing Zr content of the steels deteri-orated their mechanical property, owing to the blocky inclusions. The alloy with 0.01%Zr resulted in excellent mechanical properties due to the fine inclusions and the precipitation of Zr3V3C carbides. Values of 576 and 682 MPa were obtained for the yield strength and ultimate tensile strength of Zr-1 alloy, respectively. Furthermore, the ductile–brittle transition temperature of the alloy decreased to-85 ℃.
其他文献
RH炉耐材总承包项目较为复杂,涉及材料管理、设计、人员管理、设备操作及专业炉型的修补。良好的管理能够减少浪费、提高效率、避免事故,进而大幅降低项目成本。
The low-temperature wet oxidation behavior of semi-dry desulfurization ash from iron ore sintering flue gas in ammonium citrate solution was investigated for ef
近年来,粒子纱在花式纱线中应用得很普遍,是后继开发流行面料的基础,因此,探讨一步纺工艺完成花式纱的生产,替代传统二步纺或多步纺的工艺,实现高效、灵活纺制单色纯棉粒子纱,可提高企业的经济效益。
采用“棒磨机+V型静选+动选”这种终粉磨工艺可同时生产锅炉脱硫用石灰石粉及建筑用细砂集料。实际应用发现主产品石灰石粗粉的粒径分布较好,符合脱硫剂的粒径分布要求,证明该终粉磨工艺生产脱硫石灰石粉是可行的。
With the importance of the steelmaking industry in the economy and its negative impacts on the environment, reducing dust emissions is a vital focus in this fie
稀土(RE)微合金化是开发高品质模具钢的重要手段之一.采用稀土渣系结合电渣重熔实现H 13钢铸锭的稀土添加,重点对比研究了稀土氧化铝渣系和氧化铝渣系所制备H13钢铸锭的成分
综述了钢渣在烟气脱硫方面的利用价值并简述了脱硫原理,介绍了利用钢渣制备微晶玻璃、多孔吸声材料、新型水泥的不同方法和高附加值利用现状,并指出了钢渣利用方面的不足。
通过热模拟实验,研究了冷却工艺参数对Ti微合金化高强钢组织和硬度的影响.结果表明:当终冷温度为700℃时,随着冷却速度的增大,铁素体和珠光体组织得到了显著细化,实验钢硬度
Vanadium-bearing titanomagnetite carbon composite briquette (VTM-CCB) was proposed as an innovative and promising blast furnace burden to realize low-carbon and
以β-环糊精为壁材、桉叶精油为芯材,通过冷冻干燥法制备用于纺织品芳香及抗菌整理的桉叶精油微胶囊,分析壁芯比、包埋温度和包埋时间对桉叶精油微胶囊包埋率的影响。通过正交试验确定最佳工艺条件为β-CD浓度8g/mL、包埋温度40℃、包埋时间2h。在该条件下桉叶精油微胶囊的包埋率为72.68%,包埋效果较好。