The Li-rich Zn-doped LiNbO 3 (LN) crystals were grown by the Czochralski method. The structure of the crystals was measured by ultraviolet-visible absorption spectra. The results indicated that the Li-rich Zn-doped LN crystals had the same characteristics as the pure LN crystal. After Zn 2+ entered into the lattice of Li-rich Zn-doped LN crystal, it replaced Nb Li firstly. When there was no Nb Li , Zn 2+ replaced Li + then. The second harmonic generation (SHG) property of Li-rich Zn-doped LiNbO 3 crystal was measured. The results showed that the SHG conversation efficiency of Li-rich Zn-doped LiNbO 3 crystals was higher than that of Zn-doped LiNbO 3 crystals.
The results of that the Li-rich Zn-doped LN crystals had the same Characteristics of the pure LN crystal. After Zn 2+ entered into the lattice of Li-rich Zn-doped LN crystal, it was replaced by Nb Li first. When there was no Nb Li, Zn 2+ replaced Li + then. The second harmonic generation (SHG) property of Li-rich Zn-doped LiNbO 3 crystal was measured. The results showed that the SHG conversation efficiency of Li-rich Zn-doped LiNbO 3 crystals was higher than that of Zn-doped LiNbO 3 crystals.