采用固相烧结法制备(Bi_(0.5)Na_(0.5))0.93 Ba 0.07 Ti_(1-x)(Nb_(0.5)Cr_(0.5))x O_(3)(摩尔分数x=0%、0.5%、1%、2%、2.5%、5%)(简称BNBT-x NC)无铅压电陶瓷,研究离子对(Nb^(5+)-Cr^(3+))对0.93Bi_(0.5)Na_(0.5) TiO_(3)-0.07BaTiO_(3)(简称BNT-7BT)陶瓷微观结构、介电、铁电和应变性能的影响。结果表明,所有组分为伪立方相。随着离子对(Nb^(5+)-Cr^(3+)